OS6-08 重油燃焼ボイラにおける管の腐食減肉対策(OS6 設備診断・運用保全技術)
スポンサーリンク
概要
- 論文の詳細を見る
Tubes of the boiler firing low quality heavy oil have gotten thickness reduction due to high temperature corrosion. Corrosional characteristics of SUS347H steel, which is the material of reheaters and superheaters of the boiler, and countermeasures against this problem were investigated. Corrosion amount of SUS347H radically increased above 700℃ and has positive relativity with Po_2 in the atmosphere. Magnesium in ash effectively reduced corrosion and the requirement was the amount corresponding to MgO/V_2O_5=1. In comparing several materials, SUS310 steel was superior to SUS347H in resistivity against high temperature corrosion, and this superiority was verified by an exposure test in the actual boiler.
- 2005-06-28
著者
関連論文
- 蒸気タービン設備の余寿命診断技術に関する取組み
- OS6-4 ボイラ管肉厚測定装置の開発(OS6 設備診断・運用保全技術,循環型社会における動力エネルギー技術)
- OS6-12 蒸気タービンケーシングのクリープ疲労に関する余寿命診断研究(OS6 設備診断・運用保全技術,分散と集中の共存)
- OS6-08 重油燃焼ボイラにおける管の腐食減肉対策(OS6 設備診断・運用保全技術)
- 各機関の動向 北海道電力における火力発電設備の余寿命診断および保守技術に関する研究
- 12%Crフェライト系耐熱鋼のクリープに伴うアノード分極特性の変化
- PS28 電気化学的手法による12%Crフェライト系耐熱鋼のクリープ損傷評価の検討(フェロー賞対象ポスターセッション)