1. Four kinds of silica gel were observed to adsorb ammonia from the gas mixture made of ammonia and air or hydrogen cyanide from the gas mixture made of hydrogen cyanide and air, respectively. The adsorption rate of ammonia or hydrogen cyanide from the above mentioned gas mixtures was given, at the difinite gas pressure, to be 30-70% of the saturation quantity 10 mins. after the starting point, 70-90% 50 mins. after, and 90% ca. 100 mins. after, and then the rate gradually diminished. In this case the Sameshima equation proved to be more applicable than the others to interpret our experimental results. 2. The amount of ammonia adsorbed on silica gel increased with the decrease in temperature. The rates were 14%, 16%, 18.5%, and 21.7% by weight at 10℃, 0℃, -10℃, and -20℃, respectively, under the ammonia pressure of 0.97 atmosphere (isobar). In this case the Titoff equation proved to be able to interpret the results fairly. 3. The adsorption behaviour of the four kinds of silica gel for the isotherm did not agree with each other, and the experiment showed that they belong to the two classes of silica gel as to adsorption character. All the experimental equations proposed by Freundlich, Langmuir and B.E.T. could be applied only in special cases. In other words, any convenient equation for the isotherm applicable for all kinds of silica gel and gas has not yet been found. 4. Based on the B.E.T. equation, calculation was made as to the specific area of the gel. The results were 400 - 600m^2/g from the ammonia adsorption experiments and 300 - 500m^2/g from the hydrogen cyanide, respectively, and the heat of adsorption was ca. 2000 - 2850cal/g in the case of the ammonia adsorption and ca. 1300 - 1650cal/g in the case of the hydrogen cyanide adsorption, respectively. From the above figures of the specific area it may be assumed that gas molecules with smaller dimensions, which can penetrate into the smallest pores on the gel, increase the specific area.
- 山形大学の論文
- 1959-02-28
著者
関連論文
- メタン・アンモニア法による青酸合成研究 VI 酸化亜鉛を添加せるアルミナ系触媒について
- メタンからアセチレンの製造(V) 空気によるメタンの部分燃焼法について
- メタンと二酸化炭素から合成ガスの製造
- メタン・アンモニア法による青酸合成研究第5報 少量の白金を加えたアルミナ触媒の触媒能
- メタン・アンモニア法による青酸合成研究第4報、アルミニウム・マグネシウム2成分系触媒の触媒能について
- メタン・アンモニア法による青酸合成研究第3報、アルミニウム・マグネシウム2成分系
- メタン・アンモニア法による青酸合成研究-3〜5-
- メタン・アンモニア法による青酸合成研究 第2報, 製造法の相違による触媒能の変化等について
- シリカ・ゲルによるアンモニアおよび青酸ガスの吸着について
- メタン・アンモニア法による青酸合成研究 第1報 アルミナ触媒による基礎試験
- メタン・アンモニア・空気より青酸の製造研究 第4報 原料ガスに窒素を添加して触媒温度の低下を試みた実験
- メタン・アンモニア・空気より青酸の製造研究 第3報 白金網以外の触媒の性能を検討せる実験
- メタン・アンモニア・空気より青酸の製造研究 第2報 青酸の得量と原料ガス中のアンモニア・メタン・酸素各分圧との関係及び生成ガス中の一酸化炭素の成因に就て
- メタン・アンモニア・空気より青酸の製造研究-2〜4-
- メタン・アンモニア・空気より青酸の製造研究
- メタン・アンモニア・空気より青酸の製造研究 第1報 白金触媒を用いて行える実験