浸炭材の10^7回時間強度の定量的評価

概要

論文の詳細を見る
The fatigue strength at N=10^7 for carburized steels, which indicates the fatigue strength for specimens whose fatigue origins are not at inner defects but at as-carburized surfaces in this study, is affected by a softened structure, oxidized intergranular, retained austenite and residual stress. In the early study, it was clarified that the fatigue strength at N=10^7 of the specimens containing the retained austenite in the structure was higher than that estimated by the √<area> parameter model. This study aims to quantitatively evaluate these complex influences mentioned above and predict the fatigue strength at N=10^7 with high accuracy. Therefore, rotating bending and three point bending fatigue tests with several stress ratios were conducted using carburized SCM420s. Since the fatigue crack of all the specimens, whose fatigue origin was at the as-carburized surface, emanated from oxidized intergranular at a non-martensitic structure, the oxidized intergranular was considered to be mechanically equivalent to a surface crack. The dependence of mean stress on the fatigue strength at N=10^7 was accurately arranged by the modified Goodman diagram. Furthermore, the hardness of a thin softened structure was estimated from the half value breadth of the structure. Based on these results, the prediction of the fatigue strength at N=10^7 for the carburized SCM420s was performed by applying the √<area> parameter model, and its fatigue strength was successfully estimated at an unquestionable level for practical use.
社団法人日本機械学会の論文
2007-01-25

浸炭材の10^7回時間強度の定量的評価

スポンサーリンク

概要

著者

関連論文

スポンサーリンク