Corroison Resistivity of Amorphous Iron Alloys Containing Chromium
スポンサーリンク
概要
- 論文の詳細を見る
In order to evaluate the corrosion resistivity of amorphous iron alloys which have been characterized by outstanding mechanical properties, immersion tests and electrochemical measurements of the amorphous alloys were carried out in acidic and neutral solutions. In a 1 N NaCl solution at 30℃, 0.01-1 N HCl solutions at 30℃ and in 10% FeCl_3・6H_2O solutions at 40 and 60℃, pitting corrosion did not occur on the amorphous Fe-Cr-P-C and Fe-Cr-Ni-P-C alloys and the weight change of the alloys containing 8 at% or more Cr was not detected by a microbalance after immersing for 168 hr. The critical potential for pitting did not appear on polarization curves of the amorphous alloys and the anodic current higher than 10^<-7>A/cm^2 was not observed over the potential range 0 to 0.5 V (SCE) in 1 N NaCl and 0 to 0.9 V (SCE) in 1 M H_2SO_4 by the potentiostatic anodic polarization of the alloys containing 8 at% or more Cr. The extremely high corrosion resistivity of the amorphous iron alloys is attributed to the peculiar film formation partly by the presence of Cr and a large quantity of P in the alloys and partly by a single phase of the amorphous state.
- 東北大学の論文
著者
-
Hashimoto Koji
The Research Institute For Iron Steel And Other Metals
-
Naka M
Osaka University
-
HASHIMOTO Koji
The Research Institute for Iron, Steel and Other Metals
関連論文
- High Rate Sputtering of Corrosion-Resistant Alloys(Welding Physics, Processes & Instruments)
- Ultrasonic Brazing of Alumina to Copper Using Zn-Al Filler(Materials, Metallurgy & Weldability)
- Influence of Brazing Condition on Shear Strength of Alumina-Kovar Joint Made with Amorphous Cu_Ti_ Filler Metal
- Corrosion Behavior of Amorphous Fe-Cr-Zr Alloys
- Effect of Chromium Addition on Corrosion Resistance of Amorphous Co-Zr Alloys
- A Surface Study of Amorphous Nickel-Base Alloys Immersed in Liquid Sodium Contaminated with Impurities
- XPS and Electrochemical Studies of Effects of Metalloid Additives on Corrosion Behaviors of Amorphous Iron-Chromium Alloys
- Interfacial Microstructure and Reaction Phases in Si_3N_4/Si_3N_4 Joints Brazed with Cu-Zn-Ti Filler Alloy(Materials, Metallurgy & Weldability, INTERNATIONAL SYMPOSIUM OF JWRI 30TH ANNIVERSARY)
- 408 REACTION SYNTHESIS OF NiAl-TiC COMPOSITES AND IN-SITU JOINING TO Ni_3Al ALLOYS
- High Temperature Reactions of Ti with SiC(Materials, Metallurgy & Weldability)
- Interfacial Structure and Reaction Mechanism of SiC/Nb Joints(Materials, Metallurgy & Weldability)
- Brazing of Si_3N_4 to Metals with Al-Cu Filler Metals(Physics, Process, Instrument & Measurement)
- Brazing of Si_3N_4 to Metals with Al Filler (Report II) : Si_3N_4/Fe, Ni, Cu, Al or SUS304 Joint(Physics, Process, Instrument & Measurement)
- Brazing of Si_3N_4 to Metals with Al Filler (Report I) : Si_3N_4/Si_3N_4 and Si_3N_4/Ti or Nb Joints(Materials, Metallurgy & Weldability)
- Intermediary Layer of Titanium Oxide in Al_2O_3/Cu Joint Using Amorphous Cu-Ti Filler Metals
- Formation of Hercynite (FeAl_2O_4) at Interface of Al_2O_3/Steel Joint
- Effects of Alloying Elements on the Corrosion Behavior of Amorphous Cobalt-Base Alloys
- Effect of Molybdenum on the Corrosion Behavior of Amorphous Fe-Mo-C alloys in 1N HCl
- Surface-Activated Amorphous Alloy Fuel Electrodes for Methanol Fuel Cell
- Corrosion Behavior of Amorphous Ni-Ti-P and Ni-Cr-P Alloys
- Effect of Chromium Addition on Corrosion Resistance of Amorphous Fe-B-C and Fe-B-Si Alloys
- High Corrosion Resistance of Chromium-Bearing Amorphous Iron Alloys in Neutral and Acidic Solutions Containing Chloride
- Corroison Resistivity of Amorphous Iron Alloys Containing Chromium
- Effect of Nickel Addition on Corrosion Resistance of Amorphous Iron Base Alloys
- Corrosion Behavior of Amorphous Nickel-Valve Metal Alloys in Boiling Concentrated Nitric and Hydrochloric Acids
- An X Ray Photoelectron Spectroscopic Study of Surface Films on Amorphous Fe-Cr-Mo-P-C Alloys in 6 N HCl at 80℃
- Spontaneously Passivating Amorphous Fe-Cr-Mo-Metalloid Alloys in 6 N HCl at Room Temperature and 80℃
- Electrochemical and XPS Studies on Corrosion Behavior of Amorphous Ni-Cr-P-B alloys(Metallurgy)
- Electrochemical and XPS Studies on Corrosion Behavior of Amorphous Ni-Cr-P-B alloys
- Effect of Manganese on the Corrosion Behavior of Chromium-Bearing Amorphous Metal-Metalloid Alloys
- Thermometric Properties of Commercial Switching Diodes
- Dezincification of Alpha Brass
- Study on the Corrosion Resistivity of Al-Mg Alloys by means of a Potentiostat
- The Surface Structure of Electrodeposited Nickel
- Recent Development of Research on Amorphous Metals
- Relationship between Superlattice Structures and Electrochemical Behaviors of Copper-Gold Alloys
- Effect of the Surface Structure on the Electrochemical Behaviors of Electrodeposited Nickel
- Surface Structure and Chemical Reactivity of Electrodeposited Nickel
- Relation Between the Twin Structure and the Chemical Activity in Electrodeposited Nickel
- On the Electrochemical Behaviors of Copper-Gold Alloys
- CHARACTERISTICS OF CORROSION RESISTANT AMORPHOUS ALLOYS
- CORROSION BEHAVIOR OF AMORPHOUS ALLOYS
- The Crystallization Kinetics of Glassy Fe_ Ni_ P_