Dependence of the Growth Rate of Interstitial Loops on Irradiated Crystallographic Directions in Electron Irradiated Pure Aluminum
スポンサーリンク
概要
- 論文の詳細を見る
Pure aluminum was irradiated at 120℃ with 200 keV electrons in an electron microscope to examine the dependence of the growth rate of interstitial loop (I-loop) on the direction of incident electrons. I-loops grew proportionally with the irradiation time at 120℃. When the specimens were irradiated so that the I-loops were visible by diffraction contrasts, the growth rate depended on both directions of the incident electrons and the diffraction conditions, while it did not depend on the diffraction condition when all the I-loops were invisible. The dependence of the growth rate of I-loops on the diffraction condition may be due to the change of effective electron flux along the atomic rows by dynamic diffraction. The displacement cross section is determined by the growth rate of I-loops when all I-loops are invisible. The threshold energy profile of the fundamental triangle in pure aluminum was obtained with a combination of the steepest descent and the conjugate gradient technique.
- 社団法人応用物理学会の論文
- 1981-08-05
著者
-
Shimomura Yoshiharu
Applied Physics And Chemistry Faculty Of Engineering Hiroshima University
-
Tanaka Kunihiro
Applied Physics And Chemistry Faculty Of Engineering Hiroshima University
関連論文
- Computer Simulation of Displacement Damage Cascade Formation near Sigma 5 Twist Boundary in Silver
- Fundamental Processes of Damage Formation in Neutron-Irradiated Metals
- The Effects of Gas Atoms on the Formation of Voids in Neutron-irradiated Metals
- Effects of Low-Temperature Neutron Irradiation on T_c of LnBa_2Cu_3O_ (Ln=Y, La) and La_2CuO_4
- Types of Damages in Fission-Neutron Irradiated Cu and Cu Dilute Alloys at 200℃
- The Effects of Repeated Electron Irradiation for the Formation of Interstitial Loops in Pure Aluminum
- Molecular Dynamics Simulations of the Behavior of Small Interstitial Clusters in Copper
- Formation of Voids in Pure Aluminum Quenched in Hydrogen Gas
- Dependence of the Growth Rate of Interstitial Loops on Irradiated Crystallographic Directions in Electron Irradiated Pure Aluminum
- Point Defect Clusters at a Twin Boundary in Pure Aluminum
- On the Important Effect of Water Vapor in the Atmosphere on Void Formation in Quenched Pure Aluminum