Influences of Sb on the Growth and Properties of CuInSe_2 Thin Films

スポンサーリンク

概要

• 論文の詳細を見る

• The growth of CuInSe_2 film in the presence of an Sb beam results in a great improvement in surface morphology and grain structure. It is attributed to the surfactant modified growth caused by the Sb atoms. A p-type CuInSe_2 film with a resistivity of about 0.05 Ω-cm was obtained, which is comparable with the resistivity of a Cu-rich film grown without Sb. Photoluminescence measurements also show that the luminescence intensity of the films grown with Sb is much higher than that of the films grown without Sb having similar compositions. It is probably due to the improvement in the grain structure as well as the crystallinity within the grains.

• 社団法人応用物理学会の論文
• 1995-02-28

著者

• Lin Song-bin

  Institute Of Materials Science And Engineering National Sun Yat-sen University

• Tseng Bae-heng

  Institute Of Materials Science And Engineering National Sun Yat-sen University

• Chang Geon-Wen

  Institute of Materials Science and Engineering National Sun Yat-Sen University

関連論文

• Influences of Sb on the Growth and Properties of CuInSe_2 Thin Films

スポンサーリンク