Analysis of Deposition Selectivity in Selective Epitaxy of GaAs by Metalorganic Chemical Vapor Deposition

スポンサーリンク

概要

• 論文の詳細を見る

• In GaAs-selective epitaxy by atmospheric-pressure MOCVD using W and SiO_2 masks, the observed difference of the deposition conditions can be explained by two different mechanisms of heterogeneous nucleations (HN) on the mask surfaces. One is HN on ideally flat mask areas (case I), and the other is HN at irregular nuclei on the mask surfaces (case II). Surface concentration of reactant species on masks is analyzed by applying the surface-diffusion model to reactant species on the masks, and, for case I, the calculated results of polycrystal deposition on W and on SiO_2 masks are compared with experimental ones. It becomes apparent that the occurrence of the thick polycrystal deposition frequently observed on W masks is due to high surface concentration. Products of the surface-diffusion coefficient and the stagnantlayer thickness are estimated as 6.25 cm^3/s for W masks and 169.5 cm^3/s for SiO_2 masks at 610℃.

• 社団法人応用物理学会の論文
• 1990-11-20

著者

• OKAMOTO Kotaro

  University of Electro-Communications

• YAMAGUCHI Ko-ichi

  University of Electro-Communications

関連論文

• Zn and Si Doping in {110} GaAs Epilayers Grown by Metalorganic Chemical Vapor Deposition : Semiconductors and Semiconductor Devices
• Lateral Growth on (110) GaAs Substrates by Metalorganic Chemical Vapor Deposition : Semiconductors and Semiconductor Devices
• Selective Epitaxial Growth of AlGaAs by Atmospheric Pressure : MOCVD Using Diethylgalliumchloride and Diethylaluminiumchloride
• Atom Beam-Irradiation Effects on Selective Epitaxial Growth of GaAs by Metalorganic Chemical Vapor Deposition
• Analysis of Deposition Selectivity in Selective Epitaxy of GaAs by Metalorganic Chemical Vapor Deposition
• Spectral Shift of Photoluminescence of Highly Doped GaAs Epitaxial Layers Grown by MOCVD
• Profiling of Double-Crystal X-Ray Diffraction of InGaAs Epilayers Grown on GaAs
• Selective Epitaxial Growth on (100) Vicinal GaAs Surfaces by Atmospheric Pressure-Metalorganie Chemical Vapor Deposition Using Diethylgalliumchloride
• Lateral Growth of GaAs over SiO2 Films Prepared on (111)B Substrates by Metalorganic Chemical Vapor Deposition

スポンサーリンク