3.3 衝撃超高圧力下におけるタンタルの状態方程式計測(3. レーザー誘起衝撃波圧縮による状態方程式計測, <小特集>レーザー誘起衝撃波圧縮を用いた状態方程式研究)
スポンサーリンク
概要
- 論文の詳細を見る
We performed equation of state measurements of tantalum using laser-induced shock waves. A strong shock wave (>TPa) was generated in tantalum by the direct irradiation of laser beams from the GEKKO/HIPER glass laser system (laser wavelength λ_L=351nm, laser pulse width τ_L=2.5ns) of the ILE of Osaka University. A two-step, two-materials target, called a double-step target, was used in this experiment. The target assembly was fabricated from a base plate (aluminum or copper), a standard step (aluminum or copper), and a sample step (tantalum). The shock velocity was measured directly by observation of the emission from high temperature material or the change of the reflectivity of the rear surface of the target resulting from the arrival of the shock wave. Particle velocity and pressure were calculated using an impedance-matching technique. The obtained EOS data showed close agreement within the limits of experimental error with the extrapolation of the shock compression curve obtained by the conventional experimental shock technique.
- 社団法人プラズマ・核融合学会の論文
- 2004-06-25
著者
-
若林 邦彦
独立行政法人 産業技術総合研究所 爆発安全研究コア
-
若林 邦彦
独立行政法人 産業技術総合研究所 爆発安全研究センター 爆発衝撃研究チーム
-
若林 邦彦
独立行政法人 産業技術総合研究所 安全科学研究部門
関連論文
- 生分解性緩衝材による爆風圧低減効果
- モデル地中式火薬庫の大規模爆発実験
- (財)日本自動車研究所城里テストセンター見学記
- 熊本大学衝撃・極限環境研究センター, 日興技化(株)およびダイセル化学工業(株)播磨工場見学記
- 3.3 衝撃超高圧力下におけるタンタルの状態方程式計測(3. レーザー誘起衝撃波圧縮による状態方程式計測, レーザー誘起衝撃波圧縮を用いた状態方程式研究)
- 高速度及びフラッシュX線撮影法を用いた爆発実験における金属製容器の破片速度測定
- 衝撃加圧によるリン酸トリ-n-ブチル/発煙硝酸混合物の反応伝播
- 実大スケール防爆壁による爆風影響低減
- 砂中殉爆実験による煙火玉の同時爆発に関する研究 : 圧力測定による煙火玉の殉爆判定と騒音測定による煙火玉の殉爆個数の推定
- 砂による爆風圧低減効果
- 31m^3の水素-空気混合気体の爆轟によって発生した爆風
- 200m^3までの水素-空気混合気体の爆燃によって発生した爆風の実験的研究
- 砂を緩衝材として用いたエマルション爆薬のギャップ試験
- ゲル化水による爆風圧低減効果
- 球形煙火玉の開発現象(第1報) : 高速度撮影による煙火玉の開発現象の観察
- RDXの高圧相
- モルタル, 軽量コンクリート, 砂をギャップ材に用いた可塑性爆薬のカードギャップ試験
- 爆薬の爆発により加速される金属円板の速度
- 防爆壁周囲の爆風圧分布
- 独立行政法人 産業技術総合研究所
- 波長532nmに対するペンスリット単結晶の屈折率