THE PREPARATION OF VARIOUS n-ALKYLAMMONIUMMONTMORILLONITE-POLYACRYLONITRILE INTERCALATION COMPOUNDS AND THEIR CARBOTHERMAL REDUCTION IN N_2
スポンサーリンク
概要
- 論文の詳細を見る
Three kinds of n-CH_3 (CH_2)_nNH_3^+-montmorillonite-polyacrylonitrile intercalation compounds (n=3,5,11) were prepared and converted to nitrides to investigate the effect of the amine chain length on carbothermal reduction and the subsequent nitridation. With n=3 and 5,the similar intercalation compounds having the basal spacings of ca. 19Å were obtained. On the contrary, the intercalation compound with n=11 showed the basal spacing of 27.1Å and contained the larger amount of the organic materials than the other intercalation compounds. After the decomposition of the n-alkylammonium ions, the basal spacings of the complexes with n=3 and 5 decreased to the value corresponding to the monolayer of carbon, whereas the spacing corresponding to the multilayer of carbon was observed in the complex with n=11. By heating these intercalation compounds in N_2 at 1100-1500℃, β-sialon, AIN, and SiC formed without the crystallization of the oxides. From the intercalation compounds with n=3 and 5,β-sialon formed by the treatments above 1100℃. On heating above 1200℃, SiC was obtained. AIN was detected in the products heated above 1300℃. In spite of its greatest organic content, the intercalation compound with n=11 showed the higher threshold temperatures, indicating its lowest reactivity. Therefore, the longer amine chain was disadvantageous for nitrides formation by carbothermal reduction, since the structural conditions in the interlayer space of the intercalation compounds influenced their reactivities to a great extent.
- 日本粘土学会の論文
著者
-
KURODA KAZUYUKI
Department of Applied Chemistry, Waseda University
-
SUGAHARA Yoshiyuki
Department of Applied Chemistry, School of Advanced Science and Engineering, Waseda University
-
Kuroda Kazuyuki
Department Of Applied Chemistry And Kagami Memorial Laboratory For Materials Science And Technology
-
Kuroda Kazuyuki
Department Of Applied Chemistry School Of Science And Engineering Waseda University
-
Sugahara Yoshiyuki
Department Of Applied Chemistry School Of Advanced Science And Engineering Waseda University
-
TATO CHUZO
Department of Applied Chemistry, School of Science and Engineering, Waseda University
-
Tato Chuzo
Department Of Applied Chemistry School Of Science And Engineering Waseda University
-
Sugahara Yoshiyuki
Department of Applied Chemistry and Kagami Memorial Laboratory for Materials Science and Technology, Waseda University
関連論文
- B19 光異性化反応によるアゾベンゼン-マガディアイト層間化合物の構造変化 (第44回粘土科学討論会発表論文抄録)
- スメクタイトへの陽イオン性シアニン色素の吸着
- P21 スメクタイトへの陽イオン性シアニン色素の吸着
- B16 カオリナイト-ナイロン6層間化合物の合成 (第44回粘土科学討論会発表論文抄録)
- B16 カオリナオトーナイロン6層間化合物の合成
- A3. カオリナイト-ε-カプロラクタム層間化合物の合成 (第43回粘土科学討論会発表論文抄録)
- A3 カオリナイト-ε-カプロラクタム層間化合物の合成
- P24. ポリビニルピロリドンのカオリナイトへの直接インターカレーション (第42回粘土科学討論会発表論文抄録)
- A14.P25. カオリナイトへのβ-アラニンのインターカレーションとその層間重合 (第42回粘土科学討論会発表論文抄録)
- P24 カオリナイトへのポリビニルピロリドンの直接インターカレーション
- A14 カオリナイトへのβ-アラニンのインターカレーションとその層間重合
- カオリナイト配向膜の作製・評価
- P25 カオリナイト配向膜の作製・評価
- カオリナイト-ポリアクリルアミド層間化合物の加熱変化
- B15 カオリナイト-ポリアクリルアミド層間化合物の可燃変化
- B20.層状ケイ酸塩への非イオン性界面活性剤のインターカレーション(一般講演 口頭発表,第50回粘土科学討論会発表論文抄録)
- 層状ケイ酸塩のシリル化を利用したケイ酸骨格の精密設計
- B20 層状ケイ酸塩への非イオン性界面活性剤のインターカレーション
- A7. 有機修飾マガディアイトと有機高分子の複合化 (第43回粘土科学討論会発表論文抄録)
- A7 有機修飾マガディアイトと有機高分子の複合化
- 新規なメソ構造体-化学的合成と表面修飾を利用した展開
- 分子集合体を利用したメソポーラスマテリアルの合成
- 28p-XG-2 新規メソポーラス物質 KSW-2 の構造と生成機構
- メソポーラスマテリアルを用いた触媒設計 (高次機能触媒の設計--環境調和型触媒の開発を目指した新展開) -- (触媒の分子設計--活性サイトの設計と活性発現機構)
- 有機分子集合体を利用したメソ構造体の合成 (特集 自己組織化による無機マテリアル)
- 水溶液中におけるメチルトリエトキシシランの加水分解物の重合
- B20 層状ケイ酸塩RUB-51のシリル化反応による構造変化(口頭発表,一般講演)
- KNb_4O_6型化合物の合成及び構造
- PREPARATION OF NICKEL ALUMINUM DOUBLE HYDROXIDES FROM HEXAAMMINENICKEL (II) COMPLEX SOLUTION
- スメクタイトへのアルキルジメチルアミン-N-オキシドのインターカレーションにより得られる分子集合構造
- P20 スメクタイトへのアルキルジメチルアミン-N-オキシドのインターカレーションにより得られる分子集合構造
- スメクタイト-アルキルジメチルアミン-N-オキシド配向薄膜の合成
- 長鎖アルキルアンモニウム型フッ素四ケイ素雲母層間でのアゾベンゼンの異性化挙動
- P45 スメクタイト-アルキルジメチルアミン-N-オキシド配向薄膜の合成
- P44 長鎖アルキルアンモニウム型フッ素四ケイ素雲母層間でのアゾベンゼンの異性化挙動
- An Inorganic-Organic Hybrid Possessing a Two-dimensional Ti-O Network and Surface Ethoxy Groups Prepared via a Reaction of Titanium Oxychloride with Lithium Ethoxide
- 粘土-有機ナノコンポジット : カオリナイト-ポリビニルピロリドン層間化合物の合成
- 29 カロリナイト : アミノ酸層間化合物の合成
- 29.カオリナイト-アミノ酸層間化合物の合成(第35回粘土科学討論会発表論文抄録)
- P13 ジオール修飾カオリナイトの合成とそのアルコール分散性の調査
- Magnetically induced orientation of mesochannels inside porous anodic alumina membranes under ultra high magnetic field of 30T : Confirmation by TEM
- Synthesis of a Soluble Precursor Possessing an Nb-N Backbone Structure and Its Pyrolytic Conversion into Niobium-Based Ceramics
- Preparation of a Soluble Precursor by an Aminolysis Reaction of Zr(NEt_2)_4 and Its Pyrolytic Conversion into ZrN
- サポナイト-2, 4-Hexadiyne-1, 6-diol 層間化合物の合成
- P7 サポナイト : 2,4-Hexadiyne-1,6-diol層間化合物の合成
- INTERCALATION AND THE PHOTOCHROMISM OF AZO DYE IN THE HYDROPHOBIC INTERLAYER SPACES OF ORGANOAMMONIUM-FLUOR-TETRASILICIC MICAS
- Selective Solid-State Intercalation of cis-trans Isomers into Montmorillonite
- PREPARATION OF MONTMORILLONITE-ALKYLAMINE INTERCALATION COMPOUNDS BY SOLID-SOLID REACTIONS
- PREPARATION OF MONTMORILLONITE-POLYACRYLAMIDE INTERCALATION COMPOUNDS AND THE WATER ABSORBING PROPERTY
- Adsorption of Methylene Blue onto Aluminum-Containing Mesoporous Silica Films Prepared by Rapid Solvent Evaporation Method
- Surface modification of Mesoporous Silica to Control the States of Tris(2,2'-bipyridine)ruthenium(II) Cations
- 可溶性セラミック前駆体からの窒化アルミニウムの合成
- KCa_R_xNb_3O_(R=Nd, Sm, Gd, 及びCe)の固溶体生成及び電気的性質の希土類依存性
- 前駆体ポリ(イソプロピルイミノアラン)から合成した窒化アルミニウムのキャラクタリゼーション
- 層状Na_2Si_8O_・nH_2Oの陽イオン交換反応
- 17 層状Na_2Si_8O_17・nH_2Oの陽イオン交換反応
- 31 機能性有機分子の組織化媒体としての長鎖アルキルアンモニウム型モンモリロナイト
- 粘土鉱物からの非酸化物セラミックスの合成
- 31.機能性有機分子の組織化媒体としての長鎖アルキルアンモニウム型モンモリロナイト(第36回粘土科学 32.討論会発表論文抄録)
- ポリイソプロピルイミノアランからの窒化アルミニウムの合成(セラミック・レターズ)
- 28 モンモリロナイト : 尿素層間化合物の合成とその非線形光学効果
- 28.モンモリロナイト-尿素層間化合物の合成とその非線形光学効果(第35回粘土科学討論会発表論文抄録)
- Silica-Based Mesostructured Materials Induced by Surfactant Assemblies in the Two-Dimensionally Limited Space of a Layered Polysilicate Kanemite
- Formation of Mesoporous Silica from a Layered Polysilicate Makatite
- INCORPORATION OF THIOACETAMIDE INTO THE INTERLAYER SPACE OF MONTMORILLONITE BY SOLID-SOLID REACTIONS
- Formation of Reactive Microporous Networks from Alkoxyvinylsilylated Siloxane Cages
- AFM OBSERVATION OF KAOLINITE SURFACE USING "PRESSED"POWDER
- Adsorption of Zinc-Metallated Chlorophyllous Pigments on FSM-Type Mesoporous Silica
- PREPARATION OF A KAOLINITE-ACRYLIC ACID INTERCALATION COMPOUND AND THE HEAT-TREATED PRODUCTS
- THE CARBOTHERMAL REDUCTION PROCESS OF 2 : 1 TYPE CLAY MINERALS
- Preparation of a Hybrid Preceramic Precursor for Al-Si-C-N Nanocomposites via a Molecular Building Block Approach
- Preparation of Soluble AIN Precursors in a LiAlH_4-CH_3NH_2・HCl-(CH_3)_2NH・HCl System
- Surface Modification of Titania Particles with Urushiol (Japanese Lacquer) and Its Application to the Preparation of Polymer-Titania Hybrids
- Platinum Thin Film with a Highly Ordered Mesostructure by Contact Plating
- Preparation of Transparent Silica-Surfactant Nanocomposite Films with Controlled Microstructures
- 7 カオリナイト-ポリアクリルアミド層間化合物の不活性雰囲気下での加熱変化
- SYNTHESIS OF HEPTYLVIOLOGEN-MONTMORILLONITE-POLYMER INTERCALATION COMPOUNDS AND THEIR ELECTROCHEMICAL BEHAVIOR
- カネマイトから誘導される新規メソポーラスシリカ (特集 ナノホールアレイ材料と機能化)
- Intercalation of α,ω-Diaminoalkanes in the Interlayer Space of the Protonated Form of the Layered Perovskite H_Bi_Sr_Ta_2O_7
- THE PREPARATION OF VARIOUS n-ALKYLAMMONIUMMONTMORILLONITE-POLYACRYLONITRILE INTERCALATION COMPOUNDS AND THEIR CARBOTHERMAL REDUCTION IN N_2
- Preparation of a Kaolinite-Nylon 6 Intercalation Compound
- PREPARATION OF A KAOLINITE-ε-CAPROLACTAM INTERCALATION COMPOUND
- PREPARATION OF COBALT ALUMINUM DOUBLE HYDROXIDES BY A COPRECIPITATION METHOD
- Expansion of Intertubular Mesopores of Imogolite Nanotubes by Thermal Decomposition of an Imogolite-Poly(sodium 4-styrenesulfonate) Composite
- Formation of Hierarchically Porous Hollow Spheres Composed of Dehydroxylated Imogolite and Carbonaceous Materials
- Inorganic-Organic Layered Materials Derived via the Hydrolysis and Polycondensation of Trialkoxy(alkyl)silanes
- 化学量論及び非化学量論マグネシウムチタン酸化物スピネルの合成
- Synthesis of a Hexagonal Mesostructured Aluminophosphate
- Syntheses of Highly Ordered Mesoporous Materials, FSM-16, Derived from Kanemite
- Preparation of Inorganic-Organic Nanocomposites through Intercalation of Organoammonium Ions into Layered Silicates
- P44 層状ケイ酸塩RUB-51と層状オクトシリケートのシリル化生成物における反応性・構造上の差異(ポスター発表,一般講演)
- Ordered Silylation of Layered Silicate RUB-51 with Half-Sodalite Cages
- A Novel Preparative Method of Silica Nanotubes by Utilizing Self-assembly and Disassembly of Peptide Amphiphiles
- Synthesis of kaolinite-lactam intercalation compounds.
- Organic derivatives of layered polysilicates. II. Reaction of magadiite and kenyaite with diphenylmethylchlorosilane.
- Synthesis of layered polysilicic acid-acrylamide intercalation compounds and polymerization in the interlayer spaces.
- The effect of tetraalkylammonium ions on the distribution of the silicate anions in aqueous solutions.
- Formation of hydrotalcite-acrylate intercalation compounds and their heat-treated products.
- The preparation of alkyltrimethylammonium-kanemite complexes and their conversion to microporous materials.
- Electrochemical Preparation of Controllably Large-sized Mesoporous Platinum Films by Using Diblock Copolymers and an Organic Expander