87%Al_2O_3セラミックスのレーザ溶接によるビード特性と継手強度 : 高出力CO_2レーザによる87%Al_2O_3セラミックスの溶接(第1報)

概要

論文の詳細を見る
Fundamental characteristics of high power CO_2 laser welding of 87%Al_2O_3 ceramics were investigated with an intention to develop a joining technique for thick ceramics. It was found that a penetration depth of 20 mm is possible at a welding speed of 6.5 mm/sec and a laser power of 10 kW. The porosity ratio was lower at lower input powers, and there was a tendency that the porosity ratiodecreases with decreasing the welding speed at the same input power.The bending strength decreasedas the porosity ratio increased. Porosities, in particular large porosities at bead center, were found togreatly influence the bending strength of welded joints of alumina ceramics. The root bending strength of butt weld of 4 mm thick plate had the same value as the base material.
社団法人溶接学会の論文
1995-02-05