酸素および窒素分圧の異なる溶接雰囲気中における溶接現象と溶接部の性質(その1) : ジルコニウム合金管の溶接に関する研究(第3報)

概要

論文の詳細を見る
The purpose of this study is to investigate the influence of extremely low levels of oxygen and nitrogen partial pressure, P_<O_2> and P_<N_2> in TIG welding atmospheres on the welding phenomenon and properties of welds of zirconium alloy tubing. In TIG welding of Zircaloy-2 tubing in welding atmospheres with various P_<O_2> and P_<N_2>, the arc voltages were measured and the properties of welds (surface discoloration, oxygen and nitrogen contents) were examined. Although definite arc voltage change is not observed at welding in ≨ 4.1 Pa of P_<O_2>, a significant arc voltage drop with increase of P_<N_2> is observed at welding in 0.4〜16.9 Pa of P_<N_2>, and oxygen appears to inhibit this arc voltage drop. The surface of weld metal and heat affected zone (HAZ) in the atmosphere of 0.1 Pa of P_<O_2> and 0.4 Pa of P_<N_2> remains bright. The surface discoloration is observable slightly on weld metal and HAZ in the atmosphere of 1.1 Pa of P_<O_2> and with increase of P_<O_2> the initial straw color becomes darker until it gets partially blue. No surface discoloration is observable on weld metals and HAZ in the atmospheres of P_<N_2> ≨ 16.9 Pa with 0.1 Pa of P_<O_2>. The nitrogen content [N] in the weld metal increases linearly with increase of √<P_<N_2>>, and the increasing rate of [N] in inner part of weld metal is lower than that of [N] in outer part. The oxygen content [O] in the weld metal increases linearly with increase of √<P_<O_2>> and shows same relations as [N], although the values of [O] in the weld metals fluctuate more than [N].
社団法人溶接学会の論文
1994-05-05

酸素および窒素分圧の異なる溶接雰囲気中における溶接現象と溶接部の性質(その1) : ジルコニウム合金管の溶接に関する研究(第3報)

スポンサーリンク

概要

著者

関連論文

スポンサーリンク