片面狭開先MAG溶接法の研究(第1報) : 直流棒マイナス極性における裏波ビード形状の観察
スポンサーリンク
概要
- 論文の詳細を見る
A new technique of high efficiency one-side narrow-gap MAG welding was developed using simple I-groove and soft backing, and 'Uranami welding' was carried out easily with this technique. It is principal characteristic of this welding technique that 'Uranami welding' is carried out easily with DC electrode negative polarity. In case of high current welding, backing does not melt down because of using DC electrode negative polarity therefore high speed 'Uranami welding' can be achieved. In addition, the bead surface is U-shaped and penetration into side walls is increased owing to the change or molten metal flow in molten pool to a desirable pattern by directing control gas against the tail area of the molten pool. In this report, using mild steel plate (thickness : 22 mm) and I-groove (root gap : 10 mm) the range of welding conditions for achieving suitable 'Uranami beads' was searched for by observing many 'Uranami bead' shapes and the practical utility of this welding technique is discussed. The results are as follows ;1) Using this welding technique, suitable 'Uranami bead' is achieved easily over a wide range of welding conditions. The optimum welding conditions of this welding technique is as follows ; welding current 450 A - arc voltage 35 V - welding speed 26 cm/min wire dia. : 1.6 mm distance between contact tip-groove bottom : 35 mm primary shielding gas : 30%Ar+70%CO_2 (40l/min) secondary shielding gas : 100%CO_2 (30l/min) control gas : 80%Ar+20%CO_2 (12.5 l/min) 2) The changeable root gap range and the range of misfit of base plate within which suitable 'Uranami bead' can be achieved with this welding technique are 6〜13 mm and 0〜3 mm respectively. 3) Using this welding technique, 'Uranami bead' can be achieved without defects.
- 1985-05-05
著者
関連論文
- 狭開先内における電極ワイヤの溶融特性
- 溶接アーク周辺における探針の電流・電圧特性 : 探針による溶接開先の左右方向ならいの研究(第一報)
- 210 開先内における溶接ワイヤのずれとアーク周辺の電位との関係 : アーク現象を用いた自動ならい溶接の試み(第2報)
- 209 溶接アーク周辺の電位とその開先自動ならいへの適用 : アーク現象を用いた自動ならい溶接の試み(第1報)
- 鋼のCO_2アークスポット溶接(第2報) : アーク熱による母板の動的変形挙動
- 狭開先MAG溶接における溶込み形状の観察
- 鋼の CO_2 アークスポット溶接(第 1 報)
- 狭開先 MAG 溶接における溶滴の平均保有熱量 : 開先広さの影響
- 狭開先内における電極ワイヤの溶融特性(第 2 報) : シールドガス組成の影響
- 片面狭開先MAG溶接法の研究(第3報) : 裏波制御溶接方法の開発
- 片面狭開先MAG溶接法の研究(第2報) : 裏波ビード形状に及ぼす諸要因の影響
- 片面狭開先MAG溶接法の研究(第1報) : 直流棒マイナス極性における裏波ビード形状の観察
- MAG狭開先溶接の凝固割れ試験法と凝固割れにおよぼすボロンの影響(平成2年度春季全国大会論文発表講演論文)
- 鋼のCO_2アークスポット溶接(第3報) : 継手の特性に及ぼす板間隙の影響