金屬電弧熔着鋼の機械的性質に及ぼす熔接時に於ける冷却速度の影響 (I)
スポンサーリンク
概要
- 論文の詳細を見る
In recent years, the process of electric are welding has made very remarkable strides and has gained an important foothold in various industrial fields. A great deal of attention is now being given to the physical testing of metal deposited by the electric are and considerable research has been, and is still being done, to improve the quality of the deposited metal. One of the most important problems with which the welding engineer is comfronted is the control of the temperature of the deposited metal during the welding operation. The following reports represents the results of tensile tests of all-welded-metal which are deposited in the case of the various temperatures, heating and cooling rate of the deposited metal during the welding operation, namely, those giving changed unwelding-time between each layer in the weld. 67 kinds of mediumly coated electrodes were included in the 500 specimens tested-manganese, manganese-chrome, manganese-nickel, and manganese-nickel-chrome contained in the fluxes respectively-. In addition tensile tests on specimens turned entirely from the all deposited metal were made, from which the chemical analysis and hardness of the deposited metal, the ultimate tensile strength, the percentage elongation observed were tabulated in the order of increasing unwelding-time between a layer and layer for comparison and interpretation of results. The effect of unwelding-time are shown by grouping the specimens according to alloy element in the flux and plotting curve for each groups, with values from tensile tests for ordinates and unwelding-time between a layer and layer for abscissa. These curves (results) are shown that even if all the conditions save the unwelding-time between a layer and layer were unchanged to all tests, the ultimate tensile strength, yield pt. and percentage elongation were different. The chief conclusions that are drawn on the basis of these results are : 1) That the mechanical properties of welded metal is changed by temperature and unwelding-time between each layer (-cooling velocity of deposited metal-) of the weld metal during the welding operation. 2) That the depth of the effect of the cooling velocity of the deposited metal during the welding operation upon the mechanical properties of welded metal depends on the kinds and quantity of alloy element in the electrode used (of conrse, all the conditions are quite samely). The author wishes that these suggestions and critisisms are invited to quide further work. The writer acknowledges with thanks to the many courtesis of the Fujinagata Dock Yard Ltd. Co. for permision to publish the results. And, the present writer wishes to express his hearty thanks to H. Sasa, the chief of the department of ship building of the Fujinagata Deck Yard Ltd. Co. for his kind guidance, and to Assist. Prof. M. Okada of the Osaka Imp. Univ. for his valuable suggestions during the progress of this work.
- 社団法人溶接学会の論文
著者
関連論文
- 1 箇の圓孔を持つ矩形板の引張による表面變化と(板の厚さ/孔の直径)比との關係
- 銅-鉛合金の強さ並に引張による破損及び破壞經過に對する顯微鏡的研究
- 圓形融接栓を持つ矩形板の強さ及び伸張による破壞經過と栓の硬さとの關係に就て
- 新しき圓板電弧熔接法に就いて
- 1箇の圓孔を持つ矩形板の引張りによる表面變化と板厚に對する孔の直徑比との關係
- 銅-鉛合金の強さ並に引張りによる破損及び破壊經過に對する顯微鏡的研究
- 圓形融接栓を持つ矩形板の強さ及び伸張による破壊經過と栓の硬さとの關係に就て
- 18-8 不銹鋼の熔着部に現れる繊維状破面に就いて
- 18-8 不銹鋼全熔着金属の引張による横断面の形状變化と局部断面収縮に就いて
- 地鐵の溶體化速度より見たる熔接部の時効硬化に就いて
- 高抗張力鋼鋲の製鋲及び製鋲時に於ける加熱温度, 加熱時間及び製鋲時間に就て
- AR 管と銅製鍔との熔接及び鑞接に就いて
- 金屬電弧熔着鋼の機械的性質に及ぼす熔接時に於ける冷却速度の影響 (III)
- 金屬電弧熔着鋼の機械的性質に及ぼす熔接時に於ける冷却速度の影響 (II)
- 金屬電弧熔着鋼の機械的性質に及ぼす熔接時に於ける冷却速度の影響 (I)
- 軟鋼蕊線被覆電極棒の被覆劑中に混入する滿俺鐵が、其の膠着鐵及び鎔接々手の機械的性質と化學的組成に及ぼす影響、並に其の滿俺鐵の損失に就て (III)
- 軟鋼蕊線被覆電極棒の被覆劑中に混入する満俺鐵が、其の膠着鐵及び鎔接々手の機械的性質と化学的組成に及ぼす影響、並に其の満俺鐵の損失に就て (II)
- 軟鋼蕊線被覆電極棒の被覆劑中に混入する滿俺鐵が、其の膠着鐵及び鎔接々手の機械的性質と化学的組成に及ぼす影響、並に其の滿俺鐵の損失に就て