Ar-O_2 雰囲気における鉄溶接金属の酸素吸収について : アーク溶接過程における鉄溶接金属の酸素吸収について(第 1 報)

概要

論文の詳細を見る
Pure iron was welded in a controlled arc atmosphere. Effects of the welding conditions and the oxygen partial pressure in Ar-O_2 welding atmosphere on the oxygen content of iron weld metal were systematically studied. The results are summarized as follows : 1. The temperature of iron molten pool is measured by using a thermocouple. According to the result, the temperature is suggested to be above 1600℃-1680℃. 2. The oxygen content of iron weld metal decreases with increasing welding current and increases with increasing arc voltage (P_<O_2>=0.03atm). 3. The oxygen content of iron weld metal increases with increasing of partial pressure of oxygen under low partial pressure of oxygen in Ar-O_2 welding atmosphere. However the oxygen content becomes a constant value of about 0.24wt.% under high partial pressure of oxygen. 4. The oxygen content of weld metal is higher under electrode negative (DCRP) condition than under electrode positive (DCSP) condition. 5. Behaviour of oxygen absorption into iron weld metal is discussed by using equilibrium data.
社団法人溶接学会の論文
1983-03-05