サブマージアーク水平すみ肉溶接のビード形状について

スポンサーリンク

概要

• 論文の詳細を見る

• It is often observed that the shape of horizontal fillet weld bead is influenced by welding variables and flux. From the viewpoint of the interfacial tension phenomena, this study was done to investigate the relation among the shape of horizontal fillet weld bead, welding variables and flux composition. Firstly, a theoretical consideration on the formation of horizontal fillet weld bead was made on the assumption that the shape of weld bead would be determined by the balance of interfacial tensions between slag, molten metal and solid metal, gravity of liquid metal and so forth. Secondly, the effect of interfacial tension between slag and metal on the bead shape was examined experimentally. The interfacial tension was measured by a new method proposed in this paper. That is, flux and wire were melted by TIG arc in a copper crucible cooled with water. The interfacial tension was calculated from the shape of a frozen steel drop. The following results were obtained : (1) The shapes of horizontal fillet weld bead are classified into three types in submerged arc welding. (2) The main factor which determines the bead shape of submerged arc horizontal fillet weldindg is the interfacial tension between slag and metal. (3) In order to get a good shaped horizontal fillet bead, it is necessary to use a flux which exhibits as large values as possible of interfacial tension and specific gravity. But, according to theoretical consideration, more than 9.5mm of leg length could not be attained for the horizontal fillet bead welded in one pass. (4) It was confirmed that the interfacial tension between molten slag and molten metal was able to be measured by the shape of a frozen steel drop. (5) With the above-mentioned method, the interfacial tension between weld slag and wled metal was measured. The values of the interfacial tesion were 1250 dyne/cm for the maximum case and 750 dyne/cm for the minimum case, respectively.

• 社団法人溶接学会の論文
• 1972-06-25

著者

• 坂本 昇

  川崎製鉄技術研究所

• 坪井 潤一郎

  川崎製鉄技術研究所

• 美浦 一彦

  川崎製鉄技術研究所

関連論文

• 668 耐剥離割れにすぐれたステンレス肉盛溶接金属の開発(ステンレス鋼 (2)・2 相ステンレス鋼・微細粒, 材料, 日本鉄鋼協会第 107 回(春季)講演大会)
• 667 ステンレス肉盛溶接部の剥離割れと潜在欠陥による超音波 C-scan 像との対応(ステンレス鋼 (2)・2 相ステンレス鋼・微細粒, 材料, 日本鉄鋼協会第 107 回(春季)講演大会)
• サブマージアーク水平すみ肉溶接のビード形状について
• 241 界面張力とビード形状の関係 : 水平すみ肉サブマージアーク溶接の研究(第2報)
• 240 水平すみ肉ビードの形状に関する基礎的考察 : 水平すみ肉サブマージアーク溶接の研究(第1報)
• エレクトロスラグ溶接におけるスラグ-メタル平衡と酸素源の解析 : エレクトロスラグ溶接における冶金反応の検討(第 1 報)
• 146 サブマージアーク溶接で発生するガスについて
• 18 溶接継手に発生する拘束応力ならびに溶接割れにおよぼす予熱の影響について
• 15 スリット形溶接割れ試験片の拘束状態の検討および構造物の溶接継手との関連について

スポンサーリンク