金銀パラジウムブリッジにおけるスプルーイングと鋳巣の関係
スポンサーリンク
概要
- 論文の詳細を見る
Ag-Pd-Au alloy is commonly used in dental practice. Although a number of casting porosities are often observed on the polished surface of the one-piece cast bridge of this alloy, no definite casting methods have yet been established for eliminating porosities. In this study, the effects of spruing were investigated on the aspects of internal porosities in the one-piece cast bridge of Ag-Pd-Au alloy. A centrifugal machine was used for casting. The cast specimens were sectioned and examined by an image analyzer connected to a metallurgical microscope. The occurrence of porosities was found to depend on the distribution of the centrifugal casting force and the solidification rate of the cast alloy. They tended to concentrate at the portions where the centrifugal force was less exerted and solidification began and/or finished last in the casting. When one sprue was attached to the pontic, the solidification of the whole cast alloy proceeded so rapidly that small porosities were widely dispersed all over the bridge. The use of a reservoir could not reduce the porosities but retarded the solidification of the pontic resulting in their concentration near the occlusal surface of the pontic. When two sprues were attached, one to each of the two crowns, marked concentration of porosities was found at the joint regions between the pontic and crowns. It is probably because of the hot spot formation at those regions by the passage of a large quantity of molten alloy into the pontic as well as the smaller centrifugal pressure. When three sprues were attached, one to the pontic and to each of the two crowns, the porosities were concentrated to the pontic and joint regions with general increase in the percentage of their occupation in the whole casting. The application of a runner-bar to the two -or three- sprue method was not so effective for reducing porosities as might have been expected. The concentrated porosities appeared to be united with each other to form larger and irregular voids, while the dispersed porosities were generally smaller and roundish.
- 九州歯科学会の論文
- 1988-02-25
著者
関連論文
- B-24 金銀パラジウム合金ブリッジにおけるスプルーイングと鋳巣の関係
- 目視下鋳造での金銀パラジウム合金クラウンに及ぼす鋳造熟練度による鋳込み温度差の影響
- ハイブリッドセラミックスの摩耗に関する研究
- 支台歯形成時の切削圧の測定
- ハイブリッドセラミックスの摩耗に関する研究
- 金銀パラジウムブリッジにおけるスプルーイングと鋳巣の関係 : 主論文の要旨
- 金銀パラジウムブリッジにおけるスプルーイングと鋳巣の関係
- 8. 歯冠修復材料の衝撃滑走摩耗に関する実験的研究 (第2報)
- 9. 歯冠修復材の衝撃滑走摩耗に関する実験的研究(第 48 回九州歯科学会総会講演抄録)
- 9∿1050 歯冠修復材料の衝撃滑走摩耗に関する実験的研究
- 歯冠前装用材料の耐摩耗性について
- 九州歯科大学附属病院補綴科来院患者の統計的観察(1979∿1983 年) : 第 3 報歯冠修復物について
- 1-2-19. スプルーイングとブリッジの鋳巣発生に関する研究 : 特に金銀パラジウム合金について(第75回日本補綴歯科学会学術大会講演要旨)
- 金銀パラジウム合金の感覚的鋳込み温度の測定