鋳造時膨縮変化の異方性に関する基礎的研究
スポンサーリンク
概要
- 論文の詳細を見る
In dental casting technique, it has been said that the metal shrinkage should be fully compensated with the same amount of expansion obtained by setting and heating the investment bulk. However, some reports have recently pointed out the anisotropy and heterogeneity of the latter. So, the author measured the displacement of 'crystobalite' investment material in the casting ring and the dimensional change of 'K-metal' casting under the conditions very close to the clinical practice to know the actual circumstances of shrinkage compensation. The displacement of two inner portions of 'crystobalite' investment in the casting ring was measured along its axis by using differential transformer, of which the core was connected to a plate embeded in the investment bulk balancing by a bob so that no gravitative effect might work. Net setting expansion of the investment bulk under the plate was generally greater at higher W/P ratio and more than 3% when the ring was lined with an appropriate number of wet asbestos layers. It increased as the number of asbestos layers increased up to a certain critical value, which was lesser at higher W/P ratio. Dimensional changes of several important portions as well as volume change of crown type and MOD type castings were also evaluated with reference to those of the wax pattern. Even in case that setting expansion by itself of the investment exceeded 3%, the casting could not always become larger than the wax pattern in every portion. Although asbestos lining had remarkable enlarging effects on the dimensions along ring radius and anyhow supported the shrinkage compensation, thickness and volume of casting could almost never become larger than those of the wax pattern even with 4 layers of asbestos. Nevertheless, at least the inside dimensions of crown and MOD castings could be sufficiently larger than those of the wax pattern under certain proper conditions. Such castings could well be fit to the model. Therefore, it may be concluded that the well-fitting casting can be produced due to a favorable deformation even with considerable shrinkage as a total.
- 九州歯科学会の論文
- 1974-11-30
著者
関連論文
- 97. Enamel Hypoplasia 患者の Oral Rehabilitation の臨床例
- 歯科用Ni-Cr合金の鋳造割れとその金属学的要因
- 7. 鋳造用埋没材の走査電顕的観察 : 鋳造過程における埋没材の表面構造的変化とその粗さにつて (第56回日本補綴歯科学会抄録)
- 1.模型材の精度(第1報) : 表面の再現性(日本歯科理工学会 近畿・中四国, 九州2支部共催学術講演会)
- 19.歯科用Ni-Cr合金の鋳造割れ(日本歯科理工学会 近畿・中四国, 九州2支部共催学術講演会)
- 4. 鋳造収縮とパターンの形状(第 37 回九州歯科学会総会講演抄録)
- 鋳造時膨縮変化の異方性に関する基礎的研究
- 埋没材の膨張におよぼす練和条件の影響 : 手練和と機械練和の相異
- 鋳造窩の寸法変化に関する研究 : 第 1 報 鋳造窩の熱膨張と埋没材リングとの関係
- 歯科鋳造用埋没材に関する研究(第 1 報) : 2 水塩結晶の微細構造と表面粗サとの関係