Effect of Environment on Static Tensile and Fatigue Properties of Ni-Ti-Nb Shape Memory Alloy
スポンサーリンク
概要
- 論文の詳細を見る
Shape memory alloys(SMAs) are designed to be used as structural elements at elevated temperatures. The material used in this study was Ni-Ti-Nb SMA with a chemical composition of 51 wt% Ni, 38 wt% Ti, and 11 wt% Nb. The shape-recovery finishing temperature was around 350 K. When the material was heated from room temperature(293 K)to high temperature(561 K), the tensile strength and 0.2%-proof stress slightly decreased, while the elongation and reduction of area increased. Young's modulus increased with the temperature, up to 673 K. The fatigue strength at 561 K in air and in water was slightly higher than at 293 K in air. The fatigue limit in water was close to that in air at 561 K. The fatigue limits at 561K were about 290, 240, and 150 MPa for stress ratios of -1, 0, and 0.5 respectively. Fatigue cracks were found to initiate in the Ti-rich precipitates in the sub-surface, indicating that the fatigue strength is affected by the mean stress. The Ni-Ti-Nb SMA was found to have sufficient mechanical and fatigue strengths to be used as a structural element at elevated temperatures in water.
- 一般社団法人日本機械学会の論文
- 1999-04-15
著者
-
SHIGENAKA Naoto
Power and Industrial Systems R & D Laboratory, Hitachi. Ltd.
-
MATSUMOTO Jun
Tokyo Institute of Technology
-
Asada Yasuhide
University Of Tokyo
-
OYAMADA Osamu
Hitachi Works, Hitachi Ltd.
-
AMANO Kazuo
Mechanical Engineering Research Lab., Hitachi Ltd.
-
ENOMOTO Kunio
Mechanical Engineering Research Lab., Hitachi Ltd.
-
Amano K
Mechanical Engineering Research Lab. Hitachi Ltd.
-
Oyamada Osamu
Hitachi Works Hitachi Ltd.
-
Enomoto Kunio
Mechanical Engineering Research Lab. Hitachi Ltd.
-
Shigenaka Naoto
Power And Industrial Systems R & D Laboratory Hitachi. Ltd.
-
Matsumoto Jun
Tokyo Electric Power Company
関連論文
- Effcts of Hydrogen Peroxide on Intergranular Stress Corrosion Cracking of Stainless Steel in High Temperature Water, ( II ) Optimization of Crack Propagation Rate Measurement System
- Real-time and Direct Analysis of Pollutants in Exhaust Gas Utilizing Resonance Enhanced Multi-photon Ionization (2) : Variations of Emissions Under Test Driving Modes
- Real-time and Direct Analysis of Pollutants in Exhaust Gas Utilizing Resonance Enhanced Multi-photon Ionization (1) : Monitoring System for Real Gas Sample
- Effects of Hydrogen Peroxide on Intergranular Stress Corrosion Cracking of Stainless Steel in High Temperature Water, (I), Effects of Hydrogen Peroxide on Electrochemical Corrosion Potential of Stainless Steel
- Effect of Zirconium Addition to Austenitic Stainless Steels on Suppression of Radiation Induced Chromium Segregation at Grain Boundaries under Ion Irradiation
- Radiation Induced Segregation at Grain Boundary in an Austenitic Stainless Steel under Ion Irradiation
- Segregation Behavior Induced by Various Particle Irradiations in Austenitic Stainless Steels
- A110 Interannual variations of summer monsoon onset over Myanmar
- Effect of Environment on Static Tensile and Fatigue Properties of Ni-Ti-Nb Shape Memory Alloy
- Preventive Effect of Shot Peening on Stress Corrosion Cracking(Materials Evaluation by X-ray and Neutron Diffractions)
- ICONE11-36447 DEVELOPMENT OF TENSILE RESIDUAL STRESS REDUCTION WELDING IN AUSTENITIC STAINLESS-STEEL
- EM2-2: Time-Resolved Measurements of Aromatic Hydrocarbon in Exhaust Gas Using Resonance Enhanced Multi-Photon Ionization Method(EM: Exhaust Emission Control and Measurement,General Session Papers)