Study on Factors Controlling Low Cycle Fatigue Life
スポンサーリンク
概要
- 論文の詳細を見る
In this paper, an effective and convenient method for estimation of low cycle fatigue life based on the small-crack growth law was proposed, and the factors that control fatigue life were clarified. The main results obtained are as follows:(1)Low cycle fatigue life is controlled by three factors:crack initiation length, crack propagation limit length and relative crack growth rate. (2)Fracture in pearlitic spheroidal graphite cast iron(PDI)starts from a microshrinkage that exists on the neighboring surface in the case of a cylindrical specimen;thus, the crack initiation length in PDI is larger than that in its matrix material(0.85%carbon steel;JIS SK5). (3)Preexisting cracks originating from defects shorten the crack propagation limit length. (4)The relative crack growth rate is accelerated by the increase in crack opening displacement range near the crack tip.
- 一般社団法人日本機械学会の論文
- 1998-04-15
著者
-
Nisitani Hironobu
Department Of Mechanical Engineering Faculty Of Engineering Kyushu Sangyo University
-
MORINO Kazuhiro
Department of Mechanical and Electrical Engineering, Tokuyama College of Technology
-
NISHIMURA Futoshi
Department of Mechanical and Electrical Engineering, Tokuyama College of Technology
-
Morino Kazuhiro
Department Of Mechanical And Electrical Engineering Tokuyama College Of Technology
-
Nishimura Futoshi
Department Of Mechanical And Electrical Engineering Tokuyama College Of Technology
関連論文
- Statistical Property of Small-Crack Growth Rate in 0.21% C Steel Smooth Specimens Having Different Ferrite Grain Sizes
- Study on Factors Controlling Low Cycle Fatigue Life
- Effective Young's Modulus of a Composite Including Two Groups of Periodically Arranged Inclusions
- J-1 MECHANICAL PROPERTIES MAPPING AROUND INTERFACE OF BONDED MATERIALS USING NANOINDENTATION(Session: Interface/FEM/CAE)
- 403 Laser Surface Modification of Aluminum Alloy