く形波ポーラログラフ法でタンタル中のニオブを定量する場合の共存元素の干渉
スポンサーリンク
概要
- 論文の詳細を見る
For the square-wave(s.w.) polarographic determination of niobium in tantalum, was studied the influence of coexisting ions, such as Bi, Gr, Cu, Fe, Mo, Mn, Ni, Sb, Sn, Ti, V, W, Zr and Ta. A s.w. polarograph of Yanagimoto type PA-210 was used. The capillary characteristics (m^2/^3t^1/^6) and the drop time of DME were 2.17mg^2/^3s^<-1>/^2 and 3.75s, respectively, at -0.20V vs. Hg-pool in concn. HCl. The analytical procedure is as follows. Dissolve less than 0,2g Ta in 15ml of 1:1 HF containing several drops of concn. HNO_3, 4ml of 1:1 H_2SO_4, and 1g of (NH_4)_2O_4. Evaporate the solution on a hot plate until a syrup-like product is obtained, and heat 10min more evolving the dense fume of SO_3. After cooling the syrup-like product, add 10ml of concn. HCl to it. Dilute the solution with concn. HCl in a 25ml volumetric flask, together with an appropriate quantity of coexisting ions of different concentration, while the solution contains (1.21×10^<-4>〜4.0×10^<-5>)mol dm^<-3> ofNb. The results found are summarized as follows. (A) Influence of the added Ta for the s.w. polarographic peak height of Nb is shown by the empirical formula; h=1.6071×10^4×1.91^<n-1>i×(C_<Nb>C_<Ta>)^<1.076>(1) C_<Ta>=1.1×10^<-2>×2^<n-1>(2) h: Peak height of Nb(mm), C_<Ta>: Concentration of Ta (mol dm^<-3>), C_<Nb>: Concentration of Nb(mol dm^<-3>). The concentration of Nb in the sample is determined from the peak heights by means of these equations. (B) The determination of Nb by this method was not interfered with 200μg/g Ta of Mo, 100μg/g Ta each of Bi-Fe and Zr, 20μg/g Ta each of Cr-Sn and W, 10μg/g Ta of Ni, 8μ,g/g Ta of Ni, 4μg/g Ta of V, 2μg/g Ta of Mn, or 1μg/g Ta of Sb, but was interfered with 1μg/g Ta of Cu. (C) The concentration range of thc determination of Nb by this method was 1.7×10^<-5> mol dm^<-3> to 1.3×10^<-4> mol dm^<-3>. The lower limit of the detection of Nb by a standard addition technique was 3.2×10^<-6> mol dm^<-3>.
- 社団法人日本分析化学会の論文
- 1978-06-05
著者
関連論文
- 炭酸ナトリウム-炭酸水素ナトリウム溶離液を用いるイオンクロマトグラフィーにおけるゴーストピーク
- 熱加水分解-イオンクロマトグラフィーによるタンタル中の塩素,フッ素の同時定量
- 黒鉛炉を用いる固体金属試料の直接法によるカルシウムの原子吸光分析
- スパークソース質量分析法による高純度タンタル粉末中の不純物の定量
- 黒鉛管原子化装置を用いた無炎原子吸光法におけるふん囲気の影響
- く形波ポーラログラフ法でタンタル中のニオブを定量する場合の共存元素の干渉
- 黒鉛チューブ原子化装置を用いたこ高純度タンタル中の微量不純物の原子吸光分析
- タンタル中ニオブの高分子量アミンによる分離とMIBK-フェニルフルオロン吸光度法による定量