イオンビー・ムスパッタ法における反跳Arの鉄薄膜特性に及ぼす影響
スポンサーリンク
概要
- 論文の詳細を見る
Fe films were deposited by ion beam sputtering. The sputtering voltage V_S was set to 1200V. The angle θ_S between the normal line of the target plane and the normal line of the substrate plane was varied in the range of 10-80°. The θ_S dependence of the prperties of the Fe films and the average energy of the energetic particles, namely the sputtered atoms and the recoiled Arions were investigated in detail. The saturation magnetization 4πM_S of the films had an almost constant value of 21kG. The coercivity H_C took a minimum value of 3 Oe when θ_S was higher than 50°. It was estimated by Monte Carlo simulation that the average energy E_<Ar> of the recoiled Ar ions was approximately 300eV when θ_S was 50°. Bombardment with high-energy recoiled Ar ions improved the structure of the films and significantly reduced their coercivity. The angle of the substrate was an important parameter for the properties of films deposited by ion beam sputtering.
- 社団法人日本磁気学会の論文
- 1999-04-15
著者
関連論文
- 膜堆積中と後にArイオン衝撃を加えたFe薄膜の構造と磁気特性(薄膜)
- Arイオン衝撃処理によるイオンビームスパッタFe膜の構造と磁気特性変化(薄膜プロセス・材料,一般)
- S1105-1-3 (111)面に配向したTiN膜の摩耗特性評価(表面改質とトライボロジー1)
- RFマグネトロンスパッタ法とイオンビームスパッタ法にて作製されたNiCr薄膜の抵抗温度係数特性に及ぼす熱ひずみ効果(電子部品)
- NiCr薄膜抵抗体における熱歪と抵抗温度係数(TCR)特性(薄膜プロセス・材料, 一般)
- C-6-10 NiCrスパッタ膜の熱歪が温度抵抗特性TCRに及ぼす効果(C-6.電子部品・材料,エレクトロニクス2)
- イオンビームスパッタ法による窒素イオン衝撃を用いたFeN薄膜の作製 (薄膜)
- 窒素イオン衝撃によるFeN薄膜の作製
- イオンビームスパッタ法によるFe薄膜のAr照射効果
- ガスフロースパッタ法で作製されたZrO_2膜をバッファ層として用いたNiCr薄膜抵抗の抵抗温度係数(薄膜プロセス・材料,一般)
- C-6-2 低剛性ZrO_2バッファ層を用いたNiCr抵抗膜のTCR特性(C-6.電子部品・材料,一般講演)
- スパッタ法で作製されたNiCr薄膜の構造と抵抗温度係数(TCR)特性に及ぼす基板の表面あらさの影響(薄膜プロセス・材料,一般)
- C-6-1 NiCr抵抗体膜のZrO_2バッファ層による抵抗温度係数TCR特性の変化(C-6.電子部品・材料,一般講演)
- Arイオン衝撃処理によるイオンビームスパッタFe膜の構造と磁気特性変化
- デュアルイオンビームスパッタ法を用いたAu超薄膜の作製とその紫外域透明電極への応用
- デュアルイオンビームスパッタ法によるFe-N膜の作製とそのアニール特性
- IBS法におけるスパッタガス種の鉄薄膜特性に及ぼす影響
- イオンビー・ムスパッタ法における反跳Arの鉄薄膜特性に及ぼす影響
- イオンビームスパッタ法における反跳Arの鉄薄膜特性に及ぼす影響