756 セラミックス溶射材の高温疲労下における変形測定
スポンサーリンク
概要
- 論文の詳細を見る
High temperature fatigue (R=0) damage and deformation behaviors of SUS304 steel thermally sprayed with Al_2O_3/NiCr coating were investigated using an electronic speckle pattern interferometry (ESPI) method. Surface cracks and delamination occurred after 1×(10)^5 cycles test when σ_<max> was 202Mpa at 873K. The lengths and number of cracks or delamination largely decreased when σ_<max> or temperature decreased to 115MPa or 573K, respectively. Strain values along cracks measured with the ESPI method were much larger than other areas due to crack opening under the tensile load. The positions of strain concentration zones on strain distribution figures by ESPI method were well corresponded to those of cracks on sprayed coatings. Strain values decreased largely where local delamination occurred.
- 一般社団法人日本機械学会の論文
- 2002-09-20
著者
関連論文
- 1001 Ni-P-Al_2O_3無電解複合メッキ皮膜の作製及び耐食性・耐摩耗性評価(機械材料・材料加工I)
- 214 溶射皮膜のはく離検出に対するAE法の適用・評価(材料力学III)
- AFMによる各種材料表面でのミクロな水滴の観察および濡れ性評価
- アルミナ溶射皮膜の高温下での疲労変形・破壊挙動
- 103 セラミックス溶射材の疲労変形挙動のレーザースペックル干渉法による測定(材料力学I)
- 純クロムの表面成分および水分によるミクロな濡れ挙動
- 832 純クロムの大気中における表面状態および水分によるミクロな濡れ挙動
- WC-Co 系溶射皮膜表面に水溶液下で生成するさび中に含まれる FeWO_4の解析
- WC系溶射皮膜表面にNa_2SO_4水溶液下で生成したさびの特性
- Na_2SO_4水溶液中でWC系溶射材表面に生じたさびの解析
- WC系溶射皮膜表面のNa_2SO_4水溶液下における腐食挙動のpHによる変化
- WC系溶射皮膜のNa_2SO_4水溶液下における表面性状のpHによる変化
- WC 系溶射皮膜表面の Na_2SO_4 水溶液における腐食挙動の経時的変化
- 411 アルミナ溶射材の高温下での疲労・破壊挙動
- 305 アルミナ溶射材の高温下での疲労変形挙動
- アルミナ溶射材の高温疲労変形挙動
- 516 アルミナ溶射材の疲労変形挙動
- 623 WC系溶射材のNa_2SO_4水溶液下における腐食疲労特性(疲労強度特性)(一般セッション)
- ESPI法を用いたセラミックス溶射材の高温疲労変形の測定
- 101 Na_2SO_4 水溶液下で生じた WC 系溶射皮膜表面のさびの解析
- 215 WC 系溶射材の Na_2SO_4 水溶液下で生じたさびの解析
- WC系溶射皮膜のNa_2SO_4水溶液下での腐食皮膜特性とその解析
- 213 不働態化皮膜のESCAによる微構造解析(機械材料II)
- 756 セラミックス溶射材の高温疲労下における変形測定
- 515 セラミックス溶射材の高温下での疲労破壊
- 各種金属表面での水滴による濡れ性の原子間力顕微鏡(AFM)による評価
- 310 無電解メッキ法によるNi-P-Al_2O_3複合皮膜の作製および耐食性・耐摩耗性評価 : 溶液への粒子混入量の影響(機械材料・材料加工II)
- 422 無電解めっきを用いたNi-P-Al_2O_3複合膜の作製及び耐食性・耐摩耗性評価(力学特性(複合材料),一般セッション)