908 複合拡散浸透処理したアルミ合金の機械的特性
スポンサーリンク
概要
- 論文の詳細を見る
The compound process of the anode oxidation treatment and the nitrogen diffusion infiltration was performed to aluminum. After the iron ion is filled to minute hole formed on the anodized aluminum film, practicable hard layer including nitride was able to be formed nitrogen diffusion infiltration process. This hardness distribution on the surface hardening layer were investigated with microhardness test and X-ray diffraction was performed on surface of the hardening layer. It was understood that the amount of wear-out decreased more greatly than a past method from the result of the wear test, and was found the improvement of mechanical characteristic.
- 一般社団法人日本機械学会の論文
- 2002-08-23
著者
関連論文
- ステンレス鋼基板上に成膜したDLC/CrN多層膜の密着性評価
- CNT表面成長軸受けの開発
- 414 ガス浸硫軟窒化を施した SUS304 の表面硬化層特性
- 1010 薄膜技術の密着力信頼性評価について(表面改質による機械の高性能化)
- 1013 軟質材料における硬質薄膜の密着力評価(基調講演,関東支部 茨城講演会)
- 109 ガス浸硫軟窒化処理を施した SUS304 鋼の表面硬化層特性に及ぼす C_2H_2 ガス濃度の影響
- 420 C_2H_2 ガスを含む雰囲気でガス浸硫窒化を施した SUS304 鋼の表面硬化層特性
- ステンレス鋼の耐摩耗性と疲労強度に及ぼすガス浸硫窒化の効果
- 339 ガス浸硫窒化を施したステンレス鋼の耐摩耗性と疲労強度
- DLC複合表面改質によるアルミニウム合金の摩耗特性と疲労特性の改善
- DLC膜の摩擦特性に及ぼす硬さの影響
- 1010 UBMS 法による DLC 膜の特性と用途展開
- 第 1 部 (36) DLC による高機能化製品の開発
- 145 ガス浸硫軟窒化処理を施した SUS304 鋼の耐摩耗性
- 金型寿命向上に必要な、金型材料・熱処理・表面処理 (鍛造用金型の寿命向上対策の要因を探る(2))
- 熱処理企業の今後
- 810 軟質材料における硬質薄膜の密着力評価(第二報)
- 719 潤滑性複合皮膜の摩擦摩耗特性による機械的信頼性保証
- 908 複合拡散浸透処理したアルミ合金の機械的特性
- 1005 UBMS法によるDLC膜の機械的特性(オーガナイズドセッション : 表面改質材の機械的安全性保証)
- アルミニウム基材上への高機能化コーティング
- High Functional Coatings on Aluminum Alloy