622 A Study of Thermoforming of Textile Composite Pipe Fittings

スポンサーリンク

概要

• 論文の詳細を見る

• Thermoforming of braided thermoplastic composite tubes was carried out in order to clarify the mechanism of thermoforming process for pipe fittings such as T-shape fittings, cross fittings and three dimensional fittings. The composite tube was made of cowoven braid that consists of carbon braid and polyamide resin, and the tubes with 4-ply and initial fiber orientation 18 and 26 degrees are used in the experiment. The tube set up in a molding die was formed using internal pressure by compressed air up to 0.7 MPa under nearly melting point of the matrix. Fiber orientation, wall thickness, axial reduction and branch height after the forming are measured in order to examine the forming characteristics. The branch is formed with not only the fisherman's net effect but also with moving yarns along longitudinal direction in every forming. The results show that deformation behavior of braid is very complex. Therefore, fiber orientation through the forming is also greatly changed. As a result, the height of branch can be obtained up to 20mm in T-shape fitting. Wall thickness at branch decreases with increasing height of branch. In particular, thickness is very thin near the top of branch. Axial reduction of tube varies in circumferential direction. From these results, it is found that the complex shape fitting can be produced by thermoforming. T-shape fitting, cross fitting and three dimensional fitting are achieved by this process. It is confirmed that moving yarns along longitudinal direction plays an important role in branch forming of pipe fittings.

• 一般社団法人日本機械学会の論文

著者

• Manabe Kenichi

  Department Of Cardiology Kishiwada City Hospital

• Ozaki Junichi

  Department Of Bioresources Chemistry Faculty Of Horticulture Chiba University

• Ozaki Junichi

  Department Of Mechanical Engineering Kobe City College Of Technology

関連論文

• PJ-149 Pravastatin administration reduces contrast-induced nephropathy(Kidney/Renal circulation(05)(H),Poster Session(Japanese),The 72nd Annual Scientific Meeting of the Japanese Circulation Society)
• PJ-559 Effect of Sodium Bicarbonate on the Prevention of Contrast Induced Nephropathy in Patients Undergoing Coronary Angiography(Kidney/Renal circulation-4 (H) PJ94,Poster Session (Japanese),The 70th Anniversary Annual Scientific Meeting of the Japanese
• PE-058 Effect of Early Statin Therapy on MACE for Patients with Acute Myocardial Infarction Treated with Stent Implantation(Acute Myocardial Infarction, Clinical (Diagnosis/Treatment) 2 (IHD) : PE10)(Poster Session (English))
• Ultrasonic Measurements in the Ionic Conductor β-Ag_3SI
• Inhibitory Effects of a Fermented "Makomo" Leaf Extract on Insoluble-glucan Synthesis by Serotype c Streptococcus mutans Glucosyltransferases
• Controlling Factor of Electrocatalytic Activity of Iron-containing Carbon Materials
• 622 A Study of Thermoforming of Textile Composite Pipe Fittings
• 641 Measurement of variation in Young's modulus after large deformation and simulation of Its influence on Springback Characteristic during bending
• 521 Spring-back analysis based on microscopic measurement of deformation and material properties
• 620 A New FEM-based Determination for Material Constants of Ductile Fracture Criterion

スポンサーリンク