107 α黄銅の組合せ応力下における疲労き裂発生機構の AFM による観察
スポンサーリンク
概要
- 論文の詳細を見る
Since the surface morphology of materials can be observed with atomic-scale resolution, scanning atomic force microscopy (AFM) is a powerful technique to study mechanisms of fatigue and fracture of solid materials. In the present study, slip-band formation and fatigue crack-initiation processes in α-brass were observed by means of AFM. The depth of the intrusion drastically increased with its outgrowth to a crack. For crack-initiation from slip-band, the intrusion depth took a critical value. That is, slip distance exceeds a critical value, slip-band changes for a crack. The critical depth was almost identical between cyclic shear stress and cyclic normal stress.
著者
関連論文
- α黄銅の繰返しせん断応力下における疲労すべり帯の成長とき裂発生の AFM による観察
- 740 α黄銅の繰返しせん断応力下における疲労すべり帯の成長とき裂発生条件の AFM による観察
- 107 α黄銅の組合せ応力下における疲労き裂発生機構の AFM による観察
- 111 α黄銅粗大結晶粒材における疲労き裂発生機構のAFMによる観察(GS-3 疲労き裂の発生と伝ぱ)
- 205 金属マイクロマテリアルにおける疲労破壊機構の解明
- 340 α黄銅の繰返しせん断応力下における疲労すべり帯の成長とき裂発生条件の AFM による観察
- 109 70-30 黄銅における疲労き裂発生条件の原子間力顕微鏡による検討
- 111 マイクロマテリアルの疲労試験法の開発と交流電位差法による疲労損傷の検出
- 108 高強度アルミニウム合金の腐食疲労強度に及ぼす食塩濃度の影響
- 113 高強度アルミニウム合金における腐食疲労き裂発生機構のAFMによる観察(GS-3 疲労き裂の発生と伝ぱ)
- 506 高強度Al合金における疲労き裂発生機構のAFMによる観察(GS-3 疲労(2))
- 743 工業用純アルミニウム細線における疲労損傷の検出
- 110 金属マイクロマテリアルの疲労強度に及ぼす環境の影響