YBa_2Cu_3O_y超伝導セラミックスの冷間押出による線材の作製
スポンサーリンク
概要
- 論文の詳細を見る
In this study, YBa_2Cu_3O_y superconducting wires fabricated by cold extrusion. This process is expected to orient the grains and to produce a high J_C value of the wires. The wire samples, which were extruded with the ratios of extrusion 75, 92, 140, 234, 500 and 2000, were sintered in flowing O_2 gas. As a result, all samples were confirmed to exhibit the Meissner effect and to have TC of 85-93 K. The J_c values were increased with increasing the ratio of extrusion, and the maximum J_c value of 490 A/cm^2 was measured in liquid nitrogen. However, many pores remained in the sintered body, and the oriented grains could not be recognized from SEM micrographs since the direction of grain growth was unrestricted for the pores.
- 一般社団法人日本機械学会の論文
- 1995-08-25
著者
関連論文
- フェライト振動子の鑞付け接合強度の音響振動法による評価
- スパイラル式多層容器製造装置
- 煙火星および組成物の燃焼特性
- セラミックスのインデンテーション熱衝撃抵抗試験
- Al_2O_3-ZrO_2複合材およびZrO_2の水冷熱衝撃抵抗
- Al2O3の熱衝撃抵抗に関する研究
- Al2O3のHIP処理に対するY2O3添加の影響
- カプセルフリ-HIP焼結の緻密化プロセス
- 鋼板の球面曲げの一考察
- 押出し成形によるアルミナセラミクスについて
- PSZの強度に及ぼす焼結条件の検討
- Al2O3の焼成条件と強度
- 粘塑性理論の高温非弾性解析への適用 : 温度変動下の変形挙動解析と寿命評価
- 昇温先行カプセルフリーHIP焼結における緻密化
- Al_2O_3のカプセルフリーHIP焼結における予備焼結温度と温度先行時間の影響
- YBa_2Cu_3O_y超伝導セラミックスの冷間押出による線材の作製
- Al2O3のHIP処理雰囲気と機械的性質
- セラミックスの射出成形条件の検討
- Y1Ba2Cu3Oyの仮焼条件
- 化学機器(主として高圧容器)の破壊試験と耐圧試験
- 高圧酸素中における機器部材の発火試験
- 石油精製用高温リアクタのクリ-プ強度 (原動機小特集)
- C-6-15 傾斜をつけたGaAs基盤に成長したZnSe薄膜の特性
- 窒素不純物としてアンモニアをドープしたZnSe薄膜の特性
- 温度勾配によるバッファ層を介したZnSE薄膜成長の検討
- セレン化亜鉛のバルク結晶成長法の検討
- ZnSe薄膜への塩素による不純物添加
- MOCVD法により成長したZnSe薄膜の検討
- 電気浸透による液体集束を利用した透過光制御
- 電気浸透マイクロレンズの基礎検討
- 塩素不純物を添加したZnSe薄膜の特性
- 電気浸透マイクロレンズによる透過光制御
- 光CVD法により成長したZnSe薄膜の特性
- ZnSeダイオ-ドの青色発光の検討
- 光CVDによるZnSe薄膜成長
- 熱溶解転写記録方式の検討
- Y1Ba2Cu3OyのHIP焼結
- 電気浸透を利用した透過光制御
- C-6-6 バッファー層を入れた ZnSe 薄膜における成長層の検討
- セレン化亜鉛の光伝導特性
- マイクロコンピュ-タと自動制御
- 半導体中の不純物準位の測定
- 有限要素法によるかご形3相誘導電動機の磁界解析
- 有限要素法によるかご形3相誘導電動機の磁界解析基礎理論
- ディ-ゼル機関の自動起動装置
- SITを用いた3相誘導電動機の速度制御装置
- 活性金属法によるろう付接合フェライト磁気ひずみ振動子とその特性
- SITを用いた同期発電機の界磁電流制御装置