炭素鋼S45Cの長寿命域における腐食疲労寿命分布特性と腐食ピット成長挙動
スポンサーリンク
概要
- 論文の詳細を見る
Statistical fatigue tests in the long-life region were conducted on a medium carbon steel, S45C, in 3%NaCl solution. It was found that corrosion fatigue life distribution followed the three-parameter Weibull distribution and the scatter of fatigue life increased with decreasing stress level. Along with these fatigue tests, the growth behavior of corrosion pits was examined using a laser microscope. The distribution of corrosion pit depth followed the log-normal distribution, and the corrosion pit depth increased with increasing time or the number of stress cycles. It was confirmed that the growth of corrosion pits depended on the stress level and was enhanced with increasing stress level. Based on these results, a growth law of corrosion pits including the effect of stress level was proposed.
- 1993-09-25
論文 | ランダム
- 論点・社会福祉 日本の社会福祉はこれでいいのか--非営利民間社会福祉事業、再構築の提案(下)
- 論点・社会福祉 日本の社会福祉はこれでいいのか--非営利民間社会福祉事業、再構築の提案(上)
- 21世紀につなぐ--「敬老の日」の精神をいつまでも
- 気管支喘息の根本療法の効果判定は如何にあるべきか
- 生きがいと社会活動--老人クラブ活動の意味を考える