低温焼戻しSNCM439鋼のギガサイクル疲労特性に及ぼす繰返し速度の影響

概要

論文の詳細を見る
Fatigue tests were carried out at frequencies of 20 kHz, 600 Hz and 100 Hz for low-temperature-tempered SNCM439 steel. Ultrasonic, high-speed servohydraulic and electromagnetic fatigue test machines were used for 20 kHz, 600 kHz and 100 Hz tests, respectively. The fatigue tests showed that fatigue properties were independent of the frequencies, while fatigue lives were distributed in wide range on the S-N diagram. Almost all specimens were broken from internal Al_2O_3 inclusions of various sizes between 9 and 82 μm. Fatigue lives were found to depend on the inclusion sizes. ODA, i.e. optically dark area, was observed in all specimens broken over 10^7 cycles. ODA sizes were also independent of the frequencies. The scattered S-N diagram was found to be expressed by an unique curve by normalizing stress amplitudes σ_a with fatigue limits σ'_w estimated by Murakamis equation. The modified S-N diagram showed a clear fatigue limit between 10^9 and 10^10 cycles.
社団法人日本機械学会の論文
2002-03-25