Study on the Test Conditions of Micro-hardness

スポンサーリンク

概要

• 論文の詳細を見る

• Several experiments of micro-hardness have been performed on Al and Mg single crystal in order to clarify the effect of test conditions. The micro-hardness increased rapidly at first with the increasing of test load in the small load range, then decreased gradually and became finally independent of the test load. Such phenomena were observed in the test conditions. Firstly, it was supposed that the phenomenon of increasing micro-hardness in the small load range was caused by the external vibrations which originated from the experimental station. Secondly, it was verified that the load-dependency of micro-hardness which showed that the micro-hardness decreased with the increasing of test load was due to the heterogeneous deformation of indentation and the dissimilar indentation with respect to the indentation. So, for the micro-hardness testing it is recommended that the loading rate be kept at about 10μ/sec and the loading time of indenter kept below 10 sec.

• 一般社団法人日本機械学会の論文

著者

• Yoshino Toshio

  Musashi Institute Of Technology

関連論文

• Propagations of the Surface Fatigue Cracks in Various Kinds of Notched Specimens
• The Effect of Plate Thickness on the Fatigue Crack Propagation of Very Thin Steel Plate Specimens
• Study on the Test Conditions of Micro-hardness
• Inner Stress Analysis of Plane Woven Fiber Reinforced Plastic Laminates
• Study on the Preparatory Method of Specimens for Micro-Hardness Test

スポンサーリンク