Surface Durability of Steel Rollers : In The Cases of Case Hardened and of Nitrided Rollers

スポンサーリンク

概要

• 論文の詳細を見る

• In order to clarify the surface failure and the surface durability of surface hardened steel rollers, case-hardened and nitrided steel rollers having 60mm outside diameter were examined by a rolling contact fatigue testing machine. With case-hardened rollers, there is optimum case depth for surface durability. The surface durability of nitrided rollers spalling cracks initiate in case-hardened layer and with nitrided rollers at case-core boundary. At the locations where spalling cracks initiate, the amplitude of the ratio of share stress to Vickers hardness becomes maximum. The surface durability and rolling contact fatigue life of case-hardened and nitrided rollers can be calculated by using the equations for the relation between the relation between the maximum amplitude of this ratio and the number of cycles to surface failure.

• 一般社団法人日本機械学会の論文

著者

• Fujita Komei

  Professor Faculty Of Engineering Okayama University

• YOSHIDA Akira

  Associate Professor, Faculty of Engineering, Okayama University

• Yoshida Akira

  Associate Professor Faculty Of Engineering Okayama University

関連論文

• Study on the Scoring Resistance of Lubricating Oil in Four Ball Test : 2nd Report, Maximum Temperature on the Contact Surface
• Surface Durability of Steel Rollers : In The Cases of Case Hardened and of Nitrided Rollers

スポンサーリンク