苦土橄欖岩電融体を利用したフォルステライト並びにコーヂライト磁器について : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第7報)
スポンサーリンク
概要
- 論文の詳細を見る
Forsterite porcelains for use as electrically resistant materials for high frequency and cordierite porcelains having characteristic of low thermal expansion were prepared from the electrically fused dunite which had been obtained by the author's previous work (J. Ceram. Assc., Japan, 68 [10] 237 (1960)).Forsterite porcelain The electrically fused dunite was milled with or without additions of flux agents, such as MnO2, Ni2O3, Co3O4, Ca3(PO4)2, Mg(NH4)PO4⋅6H2O, Pb3O4, PbO⋅B2O3⋅H2O, etc., formed by dry pressing into a shape of small disk, and fired at SK 10-29 for 2 hrs. The firing temperature for obtaining the vitrified bodies was high, but its range was fairly wide, i.e., SK 16-20, even in the case without additions of the flux agents. The color of the vitrified bodies was white or pale greenish white. The ease of vitrification of the bodies increasing with the decreasing particle size of dunite, the increasing forming pressure, and also the increasing firing temperature, of which the last factor gave the most marked effect. The power factor (tan δ) become small with the advancement of sintering, and, accordingly, with the growth of the size of crystallites in the bodies. The addition of Mg(NH4)PO4⋅6H2O, Ca(PO4)2, or PbO⋅B2O3⋅H2O as the flux agent was found to be effective for lowering both the devitrification temperature and the value of power factor. The sintered bodies had the following properties; firing shrinkage 10-14%, thermal expansion coefficient 10-11×10-6, tan δ 2-9×10-4, ε approximately 7.Cordierite porcelain The pressed mixtures of the dunite and the kaolin powders with or without additions of flux agents, such as ZnO, Pb3O4, etc., were fired at SK 13-SK 18 for 2 hrs. The thermal expansion coefficient of the vitrified bodies decreased with the increasing amount of kaolin added, reaching the minimum value when the proportion of dunite and kaolin in the mixtures became 20:80. Although the range of the firing temperature for the above composition was fairly wide, i.e., SK 13-18, the use of the flux agent, such as ZnO or Pb3O4, was found to be necessary to achieve the thorough vitrification. The vitrified bodies had almost the same electrical properties as those of the conventional one.
- 社団法人日本セラミックス協会の論文
- 1961-07-01
著者
関連論文
- ラジオ・アイソトープ追跡法による非金属介在物に関する研究 : 鋼塊中の非金属介在物の成因に関する研究 I
- 熔鉄及び熔鋼の凝固点から見た最適鋳込温度
- 44 高アルミナ質炉蓋煉瓦の特性と製鋼条件との関連性 : 高アルミナ質電気炉炉蓋煉瓦の研究 I(製鋼(平炉), 日本鉄鋼協会第 56 回(秋季)講演大会講演大要)
- 16.ガラス窯蓄熱室塩基性煉瓦の損傷に関する考察 : 実験室的試験法について(研究発表講演要旨)
- 製鋼用ノツズル・ストツパー煉瓦について
- 5屯高周波誘導爐用内張材としての赤白珪石について
- 真空溶解用耐火物について
- R. I. ^Ca を使用した二, 三の実験
- 苦土橄欖岩を主体とする電融体の組織と熱的性質について : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第4報)
- 電気製鋼炉用炉床材としての苦土橄欖岩電融体と含有硫黄成分の挙動について : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第10報)
- 苦土橄欖岩電融体を主剤とした焼結体の熱的性質について : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第9報)
- 苦土橄欖岩の電融並びに電融体の組織と性質に及ぼすチタニア添加の影響 : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第8報)
- 苦土橄欖岩電融体を利用したフォルステライト並びにコーヂライト磁器について : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第7報)
- R. I. トレーサーによる苦土橄欖岩電融体の粉砕物焼結体の耐蝕性の研究 : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第6報)
- 苦土橄欖岩の電融時における飛散物について : 苦土橄欖岩電融体の組織と性質に関する基礎研究(第5報)
- 苦土橄欖岩の電融ならびに電融体の組織におよぼすアルミナなど添加の影響 : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第2報)
- 苦土橄欖岩電融体の組織に及ぼす還元剤の影響 : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第1報)