苦土橄欖岩の電融時における飛散物について : 苦土橄欖岩電融体の組織と性質に関する基礎研究(第5報)
スポンサーリンク
概要
- 論文の詳細を見る
It was pointed out in previous papers (J. Ceram. Ass., Japan, 68 [10] 237; [12] 294 (1960)) that the mol ratio, MgO/SiO2, of the substance scattered from the furnace during the operation changes with the composition of molten dunite, and for which have given some considerations on the process of scattering.This paper contains the results of the studies of scattered substance, i.e. mineral composition, change by heating, form of particles, by means of X-ray and differential thermal analysis, thereto-gravimetric, and the observations under electron microscope.The results are as follows:(1) The scattered substance was composed mainly of forsterite and periclase accompanying Si or SiC especially when the material was rich in SiO2. At the early stage of electro-melting the substance contained a large amount of amorphous and nearly amorphous substances. By heating at 700°-800°C the formation of forsterite, and at 1000°-1100°C the increase of the rate of conversion to α-cristobalite were confirmed.(2) The scattered substances contained more or less the lower oxides of Si, especially in larger amount in the early stage of electromelting.(3) The scattered substance was composed of the fine spherical and cubic particles of the size 0.05-1.5μ, although the external form changed with the composition and also with the time and the method of sampling.(4) As far as the present experiment is concerned it was observed that the scattered substance became more and more rich in MgO with the time of melting, i.e. with the elevation of furnace temperature. At the same time the powders showed the trend of becomming larger in size.(5) The unstable lower oxides contained in scattered substance was able to be converted to stable higher oxides by allowing sufficient time to contact with air or oxygen during the sampling.
- 社団法人日本セラミックス協会の論文
- 1961-05-01
著者
関連論文
- ラジオ・アイソトープ追跡法による非金属介在物に関する研究 : 鋼塊中の非金属介在物の成因に関する研究 I
- 熔鉄及び熔鋼の凝固点から見た最適鋳込温度
- 44 高アルミナ質炉蓋煉瓦の特性と製鋼条件との関連性 : 高アルミナ質電気炉炉蓋煉瓦の研究 I(製鋼(平炉), 日本鉄鋼協会第 56 回(秋季)講演大会講演大要)
- 16.ガラス窯蓄熱室塩基性煉瓦の損傷に関する考察 : 実験室的試験法について(研究発表講演要旨)
- 製鋼用ノツズル・ストツパー煉瓦について
- 5屯高周波誘導爐用内張材としての赤白珪石について
- 真空溶解用耐火物について
- R. I. ^Ca を使用した二, 三の実験
- 苦土橄欖岩を主体とする電融体の組織と熱的性質について : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第4報)
- 電気製鋼炉用炉床材としての苦土橄欖岩電融体と含有硫黄成分の挙動について : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第10報)
- 苦土橄欖岩電融体を主剤とした焼結体の熱的性質について : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第9報)
- 苦土橄欖岩の電融並びに電融体の組織と性質に及ぼすチタニア添加の影響 : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第8報)
- 苦土橄欖岩電融体を利用したフォルステライト並びにコーヂライト磁器について : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第7報)
- R. I. トレーサーによる苦土橄欖岩電融体の粉砕物焼結体の耐蝕性の研究 : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第6報)
- 苦土橄欖岩の電融時における飛散物について : 苦土橄欖岩電融体の組織と性質に関する基礎研究(第5報)
- 苦土橄欖岩の電融ならびに電融体の組織におよぼすアルミナなど添加の影響 : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第2報)
- 苦土橄欖岩電融体の組織に及ぼす還元剤の影響 : 苦土橄欖岩電融体の組織と性質に関する基礎的研究(第1報)