セラミックコーチングの接着性に関連する高温加熱による素地金属(18-8不銹鋼)の酸化について : セラミックコーチングの研究(第2報)
スポンサーリンク
概要
- 論文の詳細を見る
Owing to the large thermal expansivity of 18-8 stainless steel, it is known that some preparatory procedure is necessary in order to obtain good adherence in ceramic coating. And the author has confirmed that good adherence could be obtained by preoxidizing the base-metal at high temperature for very short time to produce a very thin film of oxides on the surface. A series of experiments was, therefore, carried on to study the behavior of base-metal in high temperature oxidation and its effect on the adherence of ceramic coating. Moreover, the author discussed the reason why the addition of small amounts of copper oxide and vanadium oxide to mill batch improved the adherence. Following conclusions were drawn from the results obtained in present investigations : ( 1 ) The pretreatment under the condition of forming an uniformly distributed so called cloudy layer on metal surface gave better adherence of ceramic coating. ( 2 ) Such improvement of adherence may be due to the uniformly distributed amorphous substance at the metal-coating interface produced by the reaction between the coating and the oxide layers on metal. ( 3 ) Without the cloudy layer the interface looks like as being composed by transparent glass covered in direct contact the metal surface, although X-ray confirmed the existence of unknown crystalline substance. This crystal did much harm to the adherence of the coating . ( 4 ) Copper oxide used as mill addition was found to be reduced to metallic copper at the interface during the firing. The small amount of oxygen liberated from copper oxide impeded the growth of above mentioned crystals. ( 5 ) In the area of the base metal coming in direct contact with the base metal it was observed that, without exception, the transformation from γ- to α-iron was occurred , during the firing.
- 社団法人日本セラミックス協会の論文
- 1962-10-01
著者
関連論文
- PbO-V_2O_5 系の相関係と系内生成化合物
- PbO-TiO_2系低融フリット釉薬の研究
- PbO-Sb_2O_3系低融フリット釉薬の研究
- B13.釉と金属間の熱起電力(研究発表講演要旨)
- B12.琺瑯焼成時に析出する3PbO・Sb_2O_5およびPbO・TiO_2の特異性について(研究発表講演要旨)
- 多結晶体粒子の2次元的形状について
- BaO-CdO-SiO_2-V_2O_5 系アルミニウム琺瑯用フリット釉の研究
- PbO-SiO_2-V_2O_5 系アルミニウム琺瑯用フリット釉の研究
- アルミニウム琺瑯表面析出結晶のアンチモン酸鉛及びチタン酸鉛の配向性
- セラミックコーチングの接着性に関連する高温加熱による素地金属(18-8不銹鋼)の酸化について : セラミックコーチングの研究(第2報)
- 不銹鋼用セラミックコーチングの接着に影響する諸因子の研究 : セラミックコーチングの研究 (第1報)
- TiC-Cr_3C_2系固溶体及び TiC-Cr_3C_2-(Ni, Co)系サーメットの対酸化性に関する研究
- 無定形シリカ球の合成とその加熱性状
- 絹雲母の加熱変化