3.5%NiCrMoV鋼の403K水中での粒界応力腐食割れ感受性の強度依存性
スポンサーリンク
概要
- 論文の詳細を見る
Rotors and discs used in low-pressure turbines must be made of a material possessing high strength, high toughness and be capable manufacturing of extremely large components. For these reasons, 3.5% NiCrMoV steel is widely used. It has been previously reported that intergranular stress corrosion cracking in this material is initiated in wet deaerated steam when the temperature reaches approximately 400 K. As no rotor and disc material with high strength and high toughness that can serve as a substitute for 3.5 NiCrMoV steel has been found, efforts to resolve this problem have been conducted to reduce material strength to lower the susceptibility to stress corrosion cracking. The purpose of this study was to elucidate a relationship between material strength and intergranular stress corrosion cracking susceptibility. SSRT was performed in a neutral atmospheric environment at a test temperature of 403 K. The results were as follows : (1) The SSRT found that, as the 0.2% offset strength decreased, the area of the intergranular fracture was reduced. For the test specimen with an 0.2% offset strength of 777 MPa, only a tiny intergranular fracture was observed ; at 0.2% offset strengths of 697 MPa and below, cracking disappeared completely. (2) From the precipitation status of the two carbides M_3C and M_7C_3 precipitated at the grain boundaries, it was found that the disappearance of the M_3C carbide coincided with the disappearance of the intergranular fracture. From this observation, it is thought that differences in composition of these carbides have an effect on the susceptibility of 3.5% NiCrMoV steel to stress corrosion cracking. (3) It was confirmed that the M_3C carbide disappears when the 0.2% offset strength is approximately 700 MPa or below, and that these materials achieve the target value for increased resistance to intergranular stress corrosion cracking in neutral environments.
- 社団法人日本材料学会の論文
- 2002-05-15
著者
関連論文
- 耐熱合金の長時間加熱過程の材質変化に及ぼす応力の影響
- 大型用SCS24鋼の強度・靱性の改良
- 高強度・高靭性16Cr-4Ni-2Coステンレス鋳鋼製ランナの性質 (大型部品用高強度・高靭性ステンレス鋳鋼の開発-2)
- 16Cr-4Ni系ステンレス鋳鋼の強度・靭性に及ぼすCo量の検討 (大型部品用高強度・高靭性ステンレス鋳鋼の開発-1)
- 559 高速増殖炉用 9Cr-2Mo 鋼極厚肉材の機械的性質及び高温性質(耐熱鋼・耐熱合金 (1), 材料, 日本鉄鋼協会第 110 回(秋季)講演大会)
- 電子ビーム溶接用高耐食2相ステンレス鋼の開発
- CrMoV鋼の383K脱気純水中でのIGSCC感受性に及ぼす焼入れ冷却速度の影響
- 693 固溶強化型 21Cr-9Mo-8Co-3W-Ni 合金の長時間加熱後の組織変化(耐熱鋼・耐熱合金, 材料, 日本鉄鋼協会第 104 回(秋季)講演大会)
- Cr_2O_3の炭熱還元機構
- 601 ガスタービン動翼用 Ni 基耐熱合金 Udimet 720 棒及び翼材の長時間安定性(耐熱鋼・耐熱合金, 性質, 日本鉄鋼協会第 102 回(秋季)講演大会)
- SUS 410J1鋼の水素脆性挙動に及ぼす析出物の影響
- 高温純水中で使用されるボルト用SCM435の応力腐食割れに及ぼす潤滑剤の影響
- 水素及びナトリウム共存下での白金の変質
- 3.5%NiCrMoV鋼の403K水中での粒界応力腐食割れ感受性の強度依存性
- タービン実機環境中でのCrMoV鋼および3.5NiCrMoV鋼の応力腐食割れ挙動