概要
- 論文の詳細を見る
The bending fracture behavior of ZrO_2-3 mo1% Y_2O_3 (PSZ) containing 0 to 12 wt% A1_2O_3 was studied with reference to the tetrogonal-to-monolinic phase transformation by three-point bending test, XRD, SEM-EDS and dilatometry. PSZ fractured at the stress just over the elastic limit. In PSZ containing A1_2O_3, on the other hand, the plastic elongation and serration phenomena were clearly observed. The resulting fracture stress increased with the addition of Al_2O_3. The grain size and density were almost independent of the addition of Al_2O_3. The segregation of both Y_2O_3 and Al_2O_3 at grain boundaries was observed in PSZ containing Al_2O_3. The different fracture modes in PSZ containing Al_2O_3 could be attributed to this grain-boundary segregation phenomena.
- 社団法人日本材料学会の論文
- 1992-05-15
著者
関連論文
- Cu-Mg合金の不連続析出速度について
- Cu-Be合金の共析反応 (〔日本伸銅協会伸銅技術研究会〕第20回講演会)
- Al-1.7mass%Li合金の低温時効における初期段階
- Cu-Be合金における共析変態の第2段階について
- Cu-2wt%Be-Co合金における不連続析出セルの体積分率に及ぼすCo含有量の影響
- Coを含むCu-Be合金における不連続析出
- Cu-Be合金における不連続析出のセル成長について
- Pb-1.5wt%Cd合金における2種の不連続析出の顕微鏡的研究
- Cu-2.1wt%Be合金における不連続析出
- 析出硬化型高Mn非磁性鋼の疲労特性
- Y-PSZの曲げ破壊挙動に及ぼすアルミナ添加の影響
- 308 SUS304ステンレス鋼とA1O50アルミニウムの摩擦圧接部組織
- 307 SUS304ステンレス鋼とA6061アルミニウム合金の摩擦圧接における接合強度支配因子
- Pb-0.5 mass% Mg 合金の時効析出
- PbおよびPb合金の透過電子顕微鏡観察