微小な疲労き裂の伝ぱに対する一つのモデル
スポンサーリンク
概要
- 論文の詳細を見る
The growth behavior of small fatigue cracks is clearly different from that of long fatigue cracks. In this paper, a growth law of small fatigue cracks is proposed based on the stochastic damage accumulation model for long fatigue crack growth. It contains the following three ~arts~ (1) The growth rate of small crack growing in a grain is proportional to some power of the process region which is limited by the grain boundary. (2) A transgranular small crack propagates into the next grain over the grain boundary, when the stress is beyond the fatigue limit. (3) A small crack growing through the noncontinuum propagation begins the continuum one, when the plastic zone size of crack tip becomes larger than the average grain size. Many experimental facts about small fatigue cracks are explained on the basis of this growth law.
- 社団法人日本材料学会の論文
- 1988-09-15
著者
関連論文
- 真空中でのガラスの静的疲労き裂伝ぱ
- 炭素繊維複合材の疲労に対する確率論的考察
- 214 炭素繊維複合材(CFRP)の疲労に対する確率論的考察(複合材料)
- 不規則進展抵抗をもつ疲労き裂進展の確率論的考察
- 進展抵抗の不規則性を考慮したクリープ き裂伝ぱ過程に対する確率論的考察
- 確率論的損傷累積モデルによるクリープき裂伝ぱ則
- 確率論的損傷累積モデルによる疲労き裂進展則(大規模降伏下でのき裂とモードII形き裂)
- 確率論的損傷累積モデルによる疲労き裂進展則
- 微小な疲労き裂の進展則
- 117 高サイクル疲労における微小き裂の進展則
- 低炭素鋼の高サイクル疲労におけるき裂発生モデル
- 微小な疲労き裂の伝ぱに対する一つのモデル
- クリープにおける微小き裂の伝ぱ則