単軸引張りのPre-Strainを受けた鋼材の組合せ応力下の疲労について(加工硬化の変化)
スポンサーリンク
概要
- 論文の詳細を見る
It is the aim of this paper to present evidences for the changes of work hardening phenomena caused during the fatigue test under repeated alternating combined stresses in virgin and tensile cold-worked mild steel specimens. Changing the grade of tensile pre-straining K, the phenomena are measured dynamically with the use of strain gate and statically the dial gage, and then the differences between both measured results are argued. The aspects of slip band produced on the surface of fatigued specimens are studied by means of electron microscope in connection with the changes of word hardening. The authors find that it is not possible to draw the S-N curve by the use of the Schenk type fatigue testing machine and this original is traced. The main conclusions from this research are as follows: (1) In the case of uniaxial tensile pre-strained steel the work hardening was saturated at an early stage of the fatigue test, and then the strength falls due to the relieving of an excess of internal stress and development of micro-crack was continued slowly up to failure. (2) In the case of annealed steel two work hardening peaks were observed and one bottom appeared between those peaks at three kinds of α respectively. The difference of stresses at the 1-st peak and the bottom decreased by changing α from 0^° to 90^°. (3) The difference of stresses measured dynamically and statically were remarkable at an early stage of all fatigue tests and it was found that the work hardening phenomenon depended on the cyclic strain rate. (4) The appearence of slip band was due to the softening of fatigue test.
- 社団法人日本材料学会の論文
- 1966-11-15
著者
関連論文
- 428 圧子押込みによる銅表面付近の変形のFEM解析(OS01-1 電子デバイス実装・電子材料と計算力学(1))(OS01 電子デバイス実装・電子材料と計算力学)
- (1-26) ストライエーション及びタイヤ・トラックに関する一考察
- SC繊維強化複合材の強度と破壊過程
- チタンクラッド鋼内の疲労き裂伝播--木村康之・金子靖雄教授に捧ぐ
- 1-28 純鉄の疲労挙動発生エネルギ限界とフラクト・グラフィ
- 1-24 鋼の回転曲げ疲労過程で発生するひずみエネルギ変化に及ぼす熱処理の影響
- 鋼の回転曲げ疲労過程で発生するひずみエネルギ変化に及ぼす温度変化の影響
- 1-11 0.49%C 構造用鋼の回転曲げ疲労過程における歪エネルギ変動に及ぼす熱処理の影響
- (1-14) 鋼の回転曲げ疲労過程で発生する歪エネルギ変化に及ぼす温度変化の影響について
- (1-13) 繰返し曲げ疲労過程で発生する歪エネルギ変化の一解析法
- 鋼の回転曲げ疲労過程で発生するひずみエネルギ変化の一解析法とその変化に及ぼすPearlite Patchの影響について
- 1-13 鋼の回転曲げ疲労過程における歪エネルギ解析
- マイククロクラックに関する考察
- 単軸引張りのPre-Strainを受けた鋼材の組合せ応力下の疲労について(加工硬化の変化)
- 3-18 エポキシ樹脂の応力凍結中における複屈折変化
- 3-30 応力凍結法における冷却過程のフリンジ変化
- 3-5 光弾性材料の力学的及び光学的リラクセーション
- 組立柱のタイロッドのねじ締結軸力解析
- 122 炭素鋼環状切欠き材における回転曲げ疲労 : 歪エネルギ変化とフラクトグラフィ
- 123 0.3% 炭素鋼切欠き材の回転曲げ疲労過程における歪エネルギ変化について
- 1-26 純鉄の組合せ応力下の疲労過程で発生する歪エネルギ変化の解析法と解析例