(α+β)黄銅引張変形試料のX線的残留応力測定
スポンサーリンク
概要
- 論文の詳細を見る
It is well known that various kinds of residual stress are found to exist in extended metal and alloy specimens by means of X-ray technique. One of them has been ascribed to the difference in the yield stress of crystals between the specimen surface and its interior(surface effect). The residual stress due to the difference in the yield stress among the crystals constituting a polycrystalline agregate has also been reported. Another one called "Gafugespannungen" has been considered to be due to the difference in the yield stress of the various phases coexisting in an alloy. As regards the "Gafugespannungen", however, only the qualitative result on steel consisting of ferrite-and cementite-phases has so far been published. The present study is designed to obtain the direct X-ray evidence for the presence of the "Gafugespannungen", As an example of the two phase alloys, (α+β)-brass rod specimens were use. They were annealed at 550℃ for 2 hr in an argon atmosphere. Having been confirmed that there exists no residual stress in an annealed state, the specimens were extended statically. The residual stress in α- and β- phases on each layer near the specimen surface was determined using sin^2φ-method. Throughout the experiments the X-ray film technique using Co-K_α characteristic radiation was adopted. The results obtained are as follows : (a) After the extension of 3% α-phase remains in compression, while, β-phase in tension. The result seems to give a direct evidence for the "Gafugespannungen". (b) In spite of the presence of the "Gefugespannungen", there exists macroscopic compressional stress on each layer near the specimen surface. This may be due to the surface effect. (c) Residual stress after 10% elongation could not be determined because of the extraordinary broadening of diffraction lines, especially of those from β-phase. The results reported here are also certified by the experiments in progress using an X-ray diffractometer, the results of which will be described elsewhere in future, together with the result concerning the dependence of residual stress values on reflecting planes.
- 社団法人日本材料学会の論文
- 1963-12-15
著者
関連論文
- 材料の科学
- 討 16 α-Fe の高温クリープにおける応力依存性(V 鉄その他 BCC 金属のクリープと格子欠陥, 第 87 回講演大会 討論会講演概要)
- α鉄およびそのMo合金の高温クリープ変形時における動的回復と加工硬化
- α黄銅の疲労変形の電顕透過観察 : 格子欠陥
- 塑性変形の電子顕微鏡による直接観察 : II α黄銅の疲労変形 : 結晶塑性・格子欠陥
- Fe-4.1at%Mo 合金の高温クリープ機構(高温の組織と強度)(耐熱鋼・耐熱合金)
- 金属の高温クリープ変形機構に関する研究の現状(高温の組織と強度)(耐熱鋼・耐熱合金)
- Fe-4.1at%Mo合金の高温クリ-プ組織
- 高温における金属の変形と転位挙動
- 金属の疲労と回復 (金属は生きている)
- 407 Fe-4.1at% Mo 合金の高温クリープ機構(耐熱鋼・耐熱合金, 性質, 日本鉄鋼協会 第 98 回(秋季)講演大会)
- Cu-Cr合金に対するAg添加の影響について (〔日本伸銅協会伸銅技術研究会〕第16回講演会)
- 討 15 BCC 金属の高温クリープについて : 鉄およびその合金を中心として(V 鉄その他 BCC 金属のクリープと格子欠陥, 第 87 回講演大会 討論会講演概要)
- 銅単結晶の高温クリープ変形組織
- 討 20 Fe-Mo および Fe-W 合金の降伏および変形応力の温度依存性について(V 鉄鋼の格子欠陥, 討論会, 日本鉄鋼協会 第 78 回(秋季)講演大会)
- (α+β)黄銅引張変形試料のX線的残留応力測定
- 引張り変形した黄銅のディフラクトメータによる残留応力測定