S45C鋼のころがり疲労試験における表面損傷
スポンサーリンク
概要
- 論文の詳細を見る
In order to clarify the behavior of pitting damage, the rolling contact fatigue tests were performed under the pure rolling and the sliding-rolling contact conditions on the annealed S45C roller specimens, and especially the surface and the cross section of roller specimens during the e rolling contact fatigue tests were observed with microscopes. The summarized results are as follows : (1) The pits develop along the forward flow formed in the subsurface layer of roller under both the pure rolling and the sliding-rolling contact conditions, and the shapes of pits are on the whole irregular in the pure rolled specimens but are fan-shaped in the sliding-rolled specimens. No subsurface origin cracks are observed in both contact conditions. (2) The damages, such as the scratching or adhesive wears, the micro-pits caused by the repetitions of the normal and tangential stresses and so on, appear on the roller surface before the formation of pits. They are observed mainly in ferrite grains. And the dislocation micro-structures of the roller surface exhibit distinct substructures at the formation of pitting cracks.
- 1973-08-15
論文 | ランダム
- 尿沈渣検査から診断におよんだ APRT 欠損症の一症例
- 尿自動分析装置(日立6800形)の導入効果について
- 120 Ι.Ι.distortion correction Softwareの検討
- 新生児TSS様発疹症 neonatal TSS-like exanthematous disease (NTED) : 第6報 : 全国新生児施設におけるNTEDの流行に関するアンケート調査 (抄録)
- 新生児TSS様発疹症NeonatalTSS-like exanthematous disease (NTED) -第6報-全国新生児施設におけるNTEDの流行に関するアンケート調査(抄録)