ランダム荷重下における溶接継手の疲労き裂伝ぱ
スポンサーリンク
概要
- 論文の詳細を見る
Fatigue crack propagation properties of welded joints under random loading were investigated in air and synthetic sea water. The fatigue crack closure did not occur for whole excursion of loading, because the stress ratio around crack tip became high due to the tensile residual stresses around crack tips. That is, the applied range of stress intensity factor coincided with the effective range of stress intensity factor. The fatigue threshold in synthetic sea water was about a half of that in air. The fatigue crack propagation rates under random loading could be well estimated by the results obtained from constant amplitude tests assuming a linear cumulative damage law. That is da/dn=C{ΔK^m_<eq >- ΔK^m_<th>}, where ΔK_<eq> ={Σ(ΔK^m_i・n_i)/Σn_i}^<1/m>, n_i=0 at Δ K_i≦ΔK_<th> or n_i=n_i at ΔK_i >ΔK_<th>.
- 社団法人日本材料学会の論文
- 1991-11-15
著者
関連論文
- 溶接きずを有する継手の極低サイクル疲労特性 : ガス導管円周溶接部の許容きず寸法の検討
- ガス導管円周溶接部における許容欠陥寸法の検討
- ホットスポット応力基準による平板構造の疲労強度評価(第一報)
- 鋼材の脆性き裂伝播・停止の力学モデル (3) : 混成型試験への適用
- (39)鋼材の脆性き裂伝播・停止の力学モデル(3) : 混成型試験への適用 : 平成8年春季講演論文概要
- 鋼材の脆性き裂伝播・停止の力学モデル(2) : 温度勾配型試験への適用
- (56)鋼材の脆性き裂伝播・停止の力学モデル(2) : 温度勾配型試験への適用 : 平成7年秋季講演論文概要
- 鋼材の脆性き裂伝播・停止の力学モデル(1) : 基礎モデルの構築
- (23) 鋼材の脆性き裂伝播・停止の力学モデル(1) : 基礎モデルの構築 : 平成7年春季講演論文概要
- 鋼材の脆性き裂伝播停止挙動に関する : 考察