ニッケルー銅合金の突合せ銀ろう継手の疲労強度
スポンサーリンク
概要
- 論文の詳細を見る
The fatigue strength of silver-filler brazed joints in nickel-copper alloys was studied along with tensile strength with emphasis on the influence of filler metal, base metal and joint clearance. The brazed joint with low-melting-point filler metal contained many large defects such as blow holes, and both tensile, so that its fatigue strength was low. The strength was high for high-melting point filler metals due to a decrease in defects. However, the fatigue strength was not so high as expected from an increase in tensile strength, because the former was more sensitive to defects than the latter. Base metal with higher elastic constants constrained the deformation of filler metal, causing the fatigue strength to increase. The effect of joint clearance on the fatigue properties did not appear clearly, because the effect of defects was much more that of joint clearance.
- 1991-10-15
論文 | ランダム
- 新駆動法による液晶の応答特性の改善
- Studies on β-Lactam Antibiotics Synthesis and Antibacterial Activity of Novel C-3 Alkyne-substituted Cephalosporins
- Synthesis and Structure-Activity Relationships of a New Orally Active Caphalosporin, FK482 and the Related Compounds
- 栽培試験用として試作した一礫耕装置
- The Increase of Biogenic Sulfate Aerosol and Particle Number in Marine Atmosphere over the Northwestern North Pacific