ボイラチューブ用9CR-1 MO-V-NB-B鋼のクリープ破断強度
スポンサーリンク
概要
- 論文の詳細を見る
In order to improve the thermal efficiency of power station, it is necessary to elevate the operation temperature and pressure of boilers. This condition usually requires the usage of a large quantity of stainless steels and superalloys, which bring in an increase in construction cost and consequently in per kW power cost. Thus, it is important to develop a new kind of steel which is economical and can be a substitute for austenitic stainless steel tubing. In the present study, the effects of molybdenium, vanadium, titanium, niobium, wolfram, cupper and boron on the creep rupture strength, workability, and weldability was developed. The chemical composition of the new steel is low carbon-9% Cr-1%Mo-0.2%V-0.3%Nb-B, and its 100 000 hr creep-rupture strength is 8.0 kg/mm^2 at 600℃.
- 社団法人日本材料学会の論文
- 1979-05-15
著者
関連論文
- 18%Cr-10%Ni 系オーステナイト鋼の高温における強度と組織におよぼす炭化物安定化元素(Ti, Nb および V)の影響
- 180 7%Cr-1%Mo 鋼のクリープ破断強度におよぼす Nb, Ti, V 添加の影響 : 中 Cr 耐熱鋼の開発に関する研究-I(高温強度・耐熱鋼, 加工・性質, 日本鉄鋼協会 第 83 回(春季)講演大会)
- ボイラ用炭素鋼および低合金鋼鋼管材のクリープ破断強度
- 高合金オーステナイトステンレス鋼のクリープ破断強度におよぼす微量 Ti, Nb 添加の影響
- 13Cr鋼-カルシウム脱酸鋼の被削性
- 18Cr-10Ni ステンレス鋼のクリープ破断強度および組織変化におよぼす C, B および N の影響
- 討 12 オーステナイト耐熱鋼の炭化物析出におよぼす V の影響(III 鋼材におよぼす V の影響, 討論会, 日本鉄鋼協会 第 78 回(秋季)講演大会)
- 高 Mn オーステナイト鋼のクリープ破断強度におよぼす Ti, Nb, V および Ti, Nb, B 添加の影響
- 高マンガン・オーステナイト耐熱鋼の開発に関する研究 : 基本組成の選定と微量 Ti, Nb 添加の影響
- 321 および 347 型鋼の長時間時効後の組織および機械的性質の変化
- 微量の Ti と Nb 添加による 304 型ステンレス鋼の高温強度の改善
- 304 および 316 型鋼の長時間時効後の組織および機械的性質の変化(鉄鋼材料の組織・性質)
- ボイラチューブ用9CR-1 MO-V-NB-B鋼のクリープ破断強度
- Ca 脱酸鋼の被削性