Monodisperse poly-α-methylstyrenes in benzene at 30.0℃ and in cyclohexane at the theta temperature of 39.0℃ have been studied. The two samples are numbered 312 for M_v=1.89×10^5 and 317 for M_v=4.79×10^5. The complex rigidity and the steady-shear viscosity have been measured by means of torsion crystals at the frequencies of 19.6kc, 39.2kc, 79.4kc and 117.7kc, and a Ubbelohde dilution type viscometer respectively. The intrinsic rigidity and the limiting relaxation time (divided by K_p) are given by the extrapolation to zero concentration. The theory of Tschoegl, extended to partially-free-draining and non-Gaussian chains respectively through h and ε, may be summarized in the dimensionless functions of intrinsic rigidity and the relaxation time factors as follows, [numerical formula] [numerical formula] where ω_s is the generalized angular frequency and λ'_p is the eigenvalue of Zimm. the numerical evaluations have been performed with a high-speed computer. In the case of benzene solutions the ε's have been derived from the steady-shear intrinsic viscosities divided by those of theta solutions using Ptitsyn's equation, and the mean value is 0.15. the dimensionless plots of intrinsic rigidity shows that the most fitting curves for the data are the theoretical ones of Tschoegl for ε=0.15 and h=10. Consequently the degree of draining h is the order of 10, and the first relaxation time factor K_1 is 0.474. Then the first limiting relaxation time (τ_1)_0's are estimated at 1.29×10^<-6> sec for 312 and 5.97×10^<-6> sec for 317. In the theta solvent of cyclohexane, ε is zero and the dimensionless plots are explained by Zimm's dispersion curves i.e. h=∞. It is the non-draining case, so that K/1=0.422, and (τ_1)_0=7.17×10^<-7> sec for 312 and (τ_1)_0=2.64×10^<-6> sec for 317. The Tschoegl theory has been quantitatively confirmed with a research in infinite dilution, and the random coil polymer is considered as partially-free-draining molecule in good solvent.
- 社団法人日本材料学会の論文
- 1967-07-15
著者
関連論文
- スチレンーブタジェン共重合体の希薄トルエン溶液の粘弾性
- ポリ-α-メチルスチレン稀薄溶液の動的粘弾性
- 鎖状高分子およびα-ヘリックス高分子希薄溶液の粘弾性
- 希薄高分子溶液の動的粘弾性の濃度およびConformation依存性
- 理想鎖高分子およびポリ-L-,コポリ-DL-アミノ酸希薄溶液の粘弾性
- ポリアミノ酸希薄溶液の動的粘弾性III : 生体物理
- 希薄高分子溶液の動的粘弾性III : 高分子
- 6p-H-13 Poly-γ-Methyl-D-Glutamate希薄溶液の動的粘彈性 II
- 5p-M-4 希薄高分子溶液の動的粘弾性 II
- Poly-γ-Methyl-D-Glutamate希薄溶液の動的粘弾性(生体物理)
- 稀薄高分子溶液の動的粘弾性の濃度依存性とintrinsic rigidity(高分子)
- 高分子電解質水溶液の粘弾性測定 : 高分子
- 12p-E-6 高分子電解質水溶液の粘彈性測定
- 準濃厚高分子溶液の粘弾性
- 高分子希薄溶液の粘弾性(I)
- 高分子希薄溶液の粘弾性(II)
- タイトル無し