ばね用ピアノ線の回転曲げ疲労強度に及ぼす液体ホーニングの効果

スポンサーリンク

概要

• 論文の詳細を見る

• This report describes the effect of liquid honing on the fatigue strength of piano wires. In this investigation, wires with diameter of 2,3, 4 and 5 mm were used. They were liquid honed under six different conditions with three sizes of glass beads, and then tested with a rotating bending fatigue tester. The results obtained are summarized as follows : (1) The surface of the liquid honed wires was smooth and dull with fine depressions. (2) The improvement in fatigue strength of liquid honed wires increased as the wire diameter decreased; it was 30% for 5 mm diameter wire, and 40% for 2 mm diameter wire. (3) To obtain maximum fatigue strength, the optimum condition of liquid honing was different for each wire diameter, i.e. the honing intensity should be kept modest for small diameter and stronger for large diameter. (4) The fatigue strength of wire is considered to be increased, mainly by the residual compression stress appearing on the honed surface layer.

• 社団法人日本材料学会の論文
• 1974-05-15

著者

• 大野 明

  神奈川県工業試験所材料部

• 大野 明

  神奈川県工業試験所

• 宮川 信勇

  神奈川県工業試験所

• 向山 美喜男

  神奈川県工業試験所

関連論文

• 日本材料学会疲労試験方法規約および同規格解説について : 規格作成のいきさつ
• 金属材料の高温疲労強度に関する研究
• 金属材料の重複繰返応力に対する疲労強度に関する研究 : 2段2重重複繰返応力に対する疲労強度
• ばね用ピアノ線の回転曲げ疲労強度に及ぼすショットピーニングの効果 : 液体ホーニングとの比較
• ばね用ピアノ線の回転曲げ疲労強度に及ぼす液体ホーニングの効果
• 実働荷重による材料の疲労に関する座談会 : 第3部 実働荷重に対する強度
• ショットピーニングの加工法の研究(第3,4報)
• ショットピーニング加工法の研究 (第1, 2報) : 実用機による実験結果
• 1-2 強力鋼ボルトの片振引張疲れ強さに関する一実験

スポンサーリンク