硬質塩ビ成形材料の衝撃試験について
スポンサーリンク
概要
- 論文の詳細を見る
In order to be equipped with necessary resources for establishing the standard (JIS) of impact testing of rigid PVC compounds, the Charpy and lzod impact testing was carried out of eight kinds. of rigid PVC compounds by various testing methods, i. e., JIS K 6745, ISO R 179 and ASTM D 256. The test specimens were machined from the compression moulding plates of 4 mm in thickness, which were made according to ISO R 293. The results obtained are summarized as follows : (1) There are rough].y proportional, relations between any two of the various impact strengths obtained from different compounds, i. e., the ratio ss・ISO・a_<kC> /JIS・a_<kC> takes roughly a constant value of a little less than 0.4, the ratio ss (e) ISO・a_<kC>/JIS・a_<kC> of about 0,3, the ratio S・ISO・a_<kC>/JIS・a_<kC> of a little over 0.4, and the ratio ASTM・a_<kI>/JIS・a_<kC> of aboUt 0.7, where JIS・a_<kC>, ss・ISO・a_<kC>, ss(e)・ISO・a_<kC> and S・ISO・a_<kC> represent Charpy impact strengths measured by JIS, standard small ISO, standard small ISO (Edgewise notch) and standard ISO Charpy impact test specimens respectively, and ASTM・a_<kI> is lzod impact strength by ASTM specimen. (2) To insure effective discrimination among the impact resistances of compounds, shallower notch in the shape of Charpy impact specimen, as in JIS specimen. is preferable to deep er notch as in ISO specimen. (3) It is found that there remain some problems to be solved, i. e., the influence of blow energy (Capacity of pendulum hammer) on the absorbed energy or on the fracture form, and no separation of fractured specimen into two halves etc., in the impact testing of modified PVC compounds such as high impact PVC compounds.
- 社団法人日本材料学会の論文
- 1970-05-15
著者
関連論文
- 311 熱可塑性プラスチックのざらつき摩耗特性の経時変化
- 310 天然暴露された熱可塑性プラスチックのざらつき摩耗特性
- 硬質塩化ビニル板のシャルピー衝撃破面について
- 硬質プラスチックのシャルピー衝撃試験に関する研究 : 第7報,シャルピー衝撃値に及ぼす試験片厚さの影響
- 317 メタクリル樹脂注型板のシャルピー衝撃値の均質性
- 307 硬質塩化ビニル板のシャルピー衝撃値の均質性
- カタサ試験機の荷重検査方法について : 測定方法の違いから生ずる荷重指示値の差異
- 238 プラスチックのシャルピー衝撃試験規格における妥当な試験片形状について
- 硬質塩ビ板ISO小形試験片によるシャルピー衝撃値について
- 硬質塩ビ板のVノッチ衝撃試験片形状とそのシャルピー衝撃値との関係
- 215 デュロメータ硬さの実態調査と標準化
- スーパフィシャル・ロックウェルかたさ測定値に及ぼす各種誤差の影響 : 第2報, ダイヤモンド圧子使用の場合
- スーパフィシャル・ロックウェルかたさ測定値に及ぼす各種誤差の影響 : (第2報, ダイヤモンド圧子使用の場合)
- 硬質塩ビ成形材料の衝撃試験について