電子管電極接続材料の研究
スポンサーリンク
概要
- 論文の詳細を見る
For the purpose of selecting materials for manufacture of electrode connector in the electron be, Ni, Ni-Mn. Ni-Cr, Ni-Fe and Ni plated Fe were examined with respect to their embrittlement by annealing them in city coal gas, to the embrittlement of the stem lead wire in the stem making process, to the decrease in insulation resistance of inter-electrodes during their life, and to e fatigue of the cathode tab in the inverted pinched cathode due to the on-off cycling test. The results are summarized as follows ; (1) Embrittlement by city coal gas firing can be evaluated by measurement of tensile strength and elongation. Embrittled Ni has low tensile strength and elongation, and its metallographic structure shows micro cracks formed along the grain boundaries. (2) Embrittlement and fracture of Ni stem lead and Ni cathode tab was caused by city coal Is firing in stem making process and in glass envelope sealing-in process. Metallographic structures of the embrittled lead wire and tab showed also micro cracks along the grain boundaries. (3) Ni-Mn, when used as cathode tab, decreased in insulation resistance of inter-electrodes during its life. But it was not the case with Ni, Ni-Cr, Ni-Fe and Ni plated Fe. (4) Ni plated Ni-Fe is recommended for the stem lead wire, because it is not embrittled and hardened by city coal gas firing, nor is it oxidized in the stern making process, nor does it wet ass. (5) 42% Ni-Fe is recommended for the cathode tab material, because it is not embrittled by city coal gas firing, nor does it decrease in insulation resistance of inter-electrodes, and it is strong resistant to fatigue.
- 社団法人日本材料学会の論文
- 1969-11-15
著者
関連論文
- 電子管電極接続材料の研究
- ジルコニア-ガラス複合体の諸性質
- 傍熱型電子管ヒータ用タングステン線の研究
- タングステン線の再結晶と抗張力に関する研究
- 小型電子管ガラス外囲器の熱衝撃試験に関する研究
- Fe-Ni-Cr系合金426の酸化の研究
- 直熱型整流管用酸化物被覆陰極の研究
- アルミナ電着の研究