人工軽量骨材コンクリートのポンプ施工
スポンサーリンク
概要
- 論文の詳細を見る
In Japan the pumping of concrete is generally in practice in the building projects to save labor because of manpower shortage in the country. But there are some problems in pumping the concrete, especially of the lightweight aggregate concrete. It is the aim of this report to present information on the above mentioned problems which has been obtained through the investigations into the practices adopted in several projects. The summaries are as follows : (1) The mix proportion of concrete is revised to some degree to make the pumping easier, although there has not yet been found a general standard. (2) In many cases, the water requirement in concrete mix is increased from 5 to 10 kg per cubic meter of concrete and also is the fine/combined aggregate ratio increased from 3 to 5%. (3) The mix proportion of cement paste in concrete which is pumped up to comparatively high places (e.g. higher than 20 m) has tendency to be increased. (4) By receiving high pressure during the pumping process, the lightweight aggregate absorbs much more water than when it is under atmospheric pressure, therefore, the workability of concrete becomes lower than what it was before the pumping. The decrease of slump is in many cases not more than 3 cm but in some cases exceeds 10 cm. (5) The entrained air increases or decreases, as the case may be, but the variation shows in many cases not more than 1%. (6) The compressive strength of concrete is also affected by pumping. In certain circumstances, there is decrease of strength, even at times at the rate of more than 10%. This phenomenon may be ascribed, though not thoroughly analyzed yet, to the water which has found its way into the lightweight aggregates during the process of the pumping, due to its pressure, and which oozes out into the bond between the aggregate and the cement paste and damages it, after the concrete is moulded. (7) Thorough irrigation of the aggregates in stock yard is effective in decreasing the amount of water to be pumped into the lightweight aggregates.
- 社団法人日本材料学会の論文
- 1969-02-15
著者
関連論文
- コンクリートのポンプ圧送に関する研究 その2 : 硬化前に圧力を受けたコンクリートの諸性質の変化
- コンクリートのポンパビリティーに関する研究 その1 : 測定装置の試作と調合への関連
- 1048 軽量骨材コンクリートをポンプ圧送する場合の問題点 : 圧力を受けた揚合の骨材の吸水性状(材料・施工)
- 人工軽量コンクリートの施工法に関する研究
- 32. レデーミクスコンクリートの運搬時間に関する調査(材料・施工関係)
- 31. レデーミクストコンクリートの品質に関する調査(材料・施工関係)
- 人工軽量骨材コンクリートのポンプ施工
- レデーミクストコンクリートによるコールドジョイントの性質
- 都市におけるレデーミクストコンクリートの輸送時間に関する研究 (II)
- 33. 最近のセメント分散剤を用いたコンクリートに関する研究(材料・施工関係)
- 31.レディミクストコンクリートに関する12の問題点(第2部(材料・施工関係))