炭素繊維強化ポリアミドのステップ昇温によるクリープ特性の評価(<特集>高分子系複合材料)
スポンサーリンク
概要
- 論文の詳細を見る
Generally, to determine the creep property of a composite material, test must be carried out continuously for about 10^3 hours under a steady condition. However, power failure, earthquake or impact may occur as obstacles. In order to avoid these problems and obtain accurate data, it is necessary to carry the test on each specimen by using a single test device and collect the data in a short term as possible. Therefore, it was tried to evaluate the creep property of a specimen by enhancing the environment temperature in a step wise manner. It was found that the influence of thermal history, such as the environment temperature and hold time of each stepwise temperature change was slight up to the last step where the creep fracture occurred. Consequently, this method is considered valid for understanding the profile of creep property.
- 社団法人日本材料学会の論文
- 1996-05-15
著者
関連論文
- 含浸不良のFRPの非破壊検査法(強化プラスチックス小特集)
- 織物状補強材を用いた複合材料の破壊挙動 : I. 内部応力分布と静的挙動
- 短繊維強化ポリエーテルエーテルケトンの引張疲労特性に及ぼす平均応力の影響(疲労)
- 短繊維強化ポリエーテルサルホンの引張疲労特性に及ぼす平均応力の影響(疲労)
- CFRPおよびCF/GF三層FRPの曲げクリープ特性に関する時間-温度換算則の適用性
- 熱可塑性プラスチックの疲労特性に及ぼす強化繊維および配向性の影響
- FRP三層ハイブリッド板のクリープ特性(強化プラスチックス小特集)
- 硬質プラスチックの平面曲げ疲労特性 : 設計データとしての総合
- 硬質プラスチックの疲労強度に及ぼす試験条件の影響
- 赤外線サーモグラフィによるCFRP複合材料の欠陥検出
- 炭素繊維強化ポリアミドのステップ昇温によるクリープ特性の評価(高分子系複合材料)
- 耐久性(クリープ,応力緩和,疲労,摩耗)