中空粒子強化複合材料の各種力学的性質の評価およびその向上のための検討(<特集>複合材料)
スポンサーリンク
概要
- 論文の詳細を見る
Hollow particle filled epoxy composites are fabricated by an ordinary molding technique. Young's modulus, tensile strength, fracture toughness and dielectric constant are measured as a function of density of the composites (i.e. wall thickness of the hollow particles). Specific strength is almost flat irrespective of the density, while specific modulus and the dielectric constant increase, and the fracture toughness simultaneously decreases with the decrease in the density. Fracture path varies from fractured particles in the case of particles with thinner shell to interfacial debonding in the case of thicker shell in the fracture toughness tests, while particle fracture is predominant in the tensile tests. In-situ observation of the material tests and finite element analyses are utilized to interpret the deformation and fracture behaviors and also to estimate the in-situ strength of silica. It is clarified by the observation that particles larger than 30μm in diameter are predominantly damaged and smaller particles less than 15μm are never fractured. Premature fracture of such coarse particles in early stage of loading is attributable to the strength properties. The in-situ strength of silica increases with the decrease in the particle diameter. According to the result of the finite element analysis, stress concentrates near inner surface along an equator under uni-axial loading, and this tendency becomes remarkable with the decrease in the wall thickness. On the other hand, interfacial stress decreases rapidly with the decrease in the wall thickness. The stress concentration along the equator is relaxed under multiaxial loading which is possible in the fracture toughness tests. All of these results indicate that elimination of the coarse particles is essential to improve the tensile properties, and that interfacial modification is effective only for toughness enhancement. SiCp reinforced Al_2O_3 and SiCp reinforced aluminum composites are also analyzed numerically to evaluate the efficiency of introducing hollow particles into ceramics and polymer materials.
- 社団法人日本材料学会の論文
- 2001-05-15
著者
-
小林 俊郎
豊橋技術科学大学生産システム工学系
-
小林 俊郎
豊橋技術科学大学
-
東原 隆
タカオカ化成工業株式会社
-
戸田 裕之
豊橋技術科学大学 生産システム工学系
-
合田 孝志
豊橋技術科学大学大学院
-
東原 隆
タカオカ化成工業(株)
-
戸田 裕之
豊橋技術科学大学
-
加賀城 央
豊橋技術科学大学生産システム工学系
-
細井 一良
豊橋技術科学大学生産システム工学系
-
伊藤 洋輔
タカオカ化成工業(株)
関連論文
- X線CTによる高精度三次元ひずみ計測のための特徴点追跡法の開発
- 表面冷間加工処理を施したAC4CHアルミニウム合金鋳物の熱機械疲労特性
- ピーニング処理を施したアルミニウム合金鋳物の熱疲労特性
- 屈折コントラストイメージングによるAl-7%Si合金鋳物の延性破壊過程の3D観察
- X線マイクロトモグラフィー像を用いたAl-Siき裂材の3Dイメージベース数値力学解析
- K吸収端差分法によるAl-Zn-Ca-Ti合金の3D元素マッピング
- フレネルゾーンプレートを用いたX線結像トモグラフィーによるAl-Ag合金中の時効析出物の3D可視化
- 粒界粒子追跡による結晶粒変形挙動の4D可視化
- アルミニウム鋳物合金のポアと力学的性質の関係
- アルミニウム合金中のミクロポアが延性破壊に及ぼす影響