立方晶ペロブスカイト型Sr(Mn_<1-X>Nb_x)O_3のMnリッチ領域での電気特性(<特集>イノベーティブセラミックス(I))
スポンサーリンク
概要
- 論文の詳細を見る
Cubic perovskite-type (Mn_<1-X>Nb_x)O_3 (0.03≤x≤0.2) was synthesized by a standard ceramic technique. The cell constant increased linearly with increasing jc. Sr (Mn_<0.97>Nb_<0.03>) O_3 (x = 0.03) exhibited a metal-insulator transition at ca. 390 K, whereas Sr(Mn_<1-X>Nb_x)O_3 (0.05≤x≤0.2) was an n-type semiconductor in a temperature range of 80-773 K. From the magnetic measurement, it is obvious that the metal-insulator transition was caused by the change in the spin state of the Mn^<3+> ion. The Seebeck coefficient of Sr(Mn_<1-X>Nb_x)O_3 (0.03≤x≤0.2) was negative and showed no significant difference in the composition.
- 社団法人日本セラミックス協会の論文
- 2005-01-01
著者
関連論文
- RZnSi化合物の熱電能
- R_2Zr_2O_7と(R_1-xEu_x)_2Zr_2O_7の結晶構造と蛍光特性
- RMnSi(R=Ce, Nd, Sm)の合成と磁気的電気的性質
- 3B36 (R_Eu_x)_2M_2O_7 (R=La, Y, Gd; M=Sn, Zr) の合成と蛍光特性
- RSi2の自己燃焼合成と電磁気的性質〔英文〕
- Y-Ba-Cu-F-O系超伝導セラミックスの電磁気的性質
- セラミックス蛍光体
- 四層構造をとる六方晶系(Sr_Ba_x)MnO_3 (0.0≤x≤0.5))の合成とその性質
- Ruddlesden-Popper Ca_(Mn_V_x)_nO_ (n=2) 化合物粉体の調製と焼結体の熱電特性
- ガラス/ZrW2O8複合材料の作製と熱膨張特性
- 化学強化ガラスの信頼性に及ぼす溶融塩温度の効果
- 立方晶ペロブスカイト型Sr(Mn_Nb_x)O_3のMnリッチ領域での電気特性(イノベーティブセラミックス(I))
- 解説 ゼーベック係数測定装置 (機器特集)
- 放電プラズマ焼結法により作製したMnドープβ-FeSi_2の熱電特性
- 放電プラズマ焼結法による緻密な鉄ケイ化物の作製
- FeとSi粉末の固相反応による鉄ケイ化物の合成
- SiO2-Al2O3-K2O-Na2O系に生成するリュ-サイトの転移温度と熱膨張
- KAlSi2O6・Li2SiO3・nSiO2ガラスセラミックスの熱膨張特性
- 2H07 FeSi_2 の熱電特性に及ぼすドーピング効果
- 2A03 FeSi_x の電気的性質
- 2B20 Cr ドープした FeSi_2 のホール効果
- 2B35 遷移金属ケイ化物の燃焼合成
- ゾル-ゲル法および水熱法を用いたジルコンの合成におけるバナジウムの添加効果
- 熱電セラミックス
- ケイ化物の燃焼合成
- 電子スピン共鳴装置
- 磁性体の性質と磁気天秤測定
- 3成分系希土類第1遷移金属金属ケイ化物の合成と磁気的性質に関する研究
- 双晶構造を含む酸素欠損型LaMnO_の高分解能電子顕微鏡観察
- 傾斜ペロブスカイトの電気特性
- 高強度(σ_b≧1GPa)と強靱性(K_≧20MPa・m^)を同時に実現したパルス通電加圧焼結法(PECPS)によるアルミナ固溶ジルコニアセラミックスの作製
- RMn2Si2(R=Y,Nd,Gd)とYNi2Si2の合成と磁性